Nitrogen Vacancy Engineering in Graphitic Carbon Nitride for Strong, Stable, and Wavelength Tunable Electrochemiluminescence Emissions
Rui Zou,Yanjun Lin,Chao Lu
DOI: https://doi.org/10.1021/acs.analchem.0c05027
IF: 7.4
2021-01-18
Analytical Chemistry
Abstract:As an attractive electrochemiluminescence (ECL) emitter, graphitic carbon nitride (CN) still suffers from weak and unstable ECL signals for its poor conductivity and the occurrence of electrode passivation. In this study, a simple nitrogen vacancy (NV) engineering strategy has been developed for the improvement of ECL performances (intensity and stability) for the first time. In comparison to pristine CN (RSD = 51.98% for 10 continuous scan), ca. 60 times amplification in ECL intensity and 70 times enhancement in ECL efficiency for CN modified with NVs (CN-NVs) were obtained. In addition, more stable ECL emissions (RSD = 0.53%) were achieved for CN-NV-550 by thermal treatment of pristine CN in a N<sub>2</sub> atmosphere for another 2 h at 550 °C. The mechanism study for the vital role of NVs on the ECL of CN-NVs revealed that NVs can not only facilitate electron transfer to amplify the ECL intensity but also serve as the electron trap to inhibit electrode passivation. More interestingly, a series of CN-NVs exhibited a tunable ECL wavelength range from 470 to 516 nm with different NV contents. Moreover, their ECL spectra showed an obvious red-shift of the wavelength with their corresponding fluorescence spectra. These findings confirmed that the ECL emissions of CN-NVs were susceptible to the relevant surface states of NVs. Our work may open up a promising pathway for improving ECL performances of CN and create new possibilities for multitarget simultaneous detection based on ECL and construction of color tunable light-emitting devices.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.analchem.0c05027?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.analchem.0c05027</a>.Amperometric <i>Q</i>–<i>t</i> curve for ECL reaction of Ru(bpy)<sub>3</sub>Cl<sub>2</sub>, pristine CN, and CN-NV-500; <i>I</i><sub>ECL</sub>–times curves of Ru(bpy)<sub>3</sub>Cl<sub>2</sub>, pristine CN, and CN-NV-500 that were used for calculating total number of photons; comparison of ECL efficiencies of different nanoparticle-based ECL emitters; SEM images of (A) CN-NV-400, (B) CN-NV-500, (C) CN-NV-600, and (D) CN-NV-620; different atom contents derived from EA of pristine CN and CN-NVs with different NV contents; XPS spectra of C 1s for pristine CN, CN-NV-550, and CN-NV-620; XPS spectra of C 1s for pristine CN-400, CN-NV-500, and CN-NV-600; XPS spectra of C 1s for pristine CN-400, CN-NV-500, and CN-NV-600; peak area ratio of N<sub>2C</sub> and N<sub>3C</sub> groups of pristine CN and CN-NVs with different NV contents from XPS analysis; <i>I</i><sub>ECL</sub>–time curves of pristine CN and CN-NVs with different NV content-modified GCE in the presence of 0.02 M TEA in the voltage range from 0 to 2 V at a scan rate of 0.1 V/s; stability of ECL emission at CN-NV-400, CN-NV-500, CN-NV-600, and CN-NV-620 under 10 continuous CV scan; FL spectrum (red line), ECL emission spectrum (black line), and smoothed ECL emission spectrum (blue line) for CN-NV-400; FL spectrum (red line), ECL emission spectrum (black line), and smoothed ECL emission spectrum (blue line) for CN-NV-500; FL spectrum (red line), ECL emission spectrum (black line), and smoothed ECL emission spectrum (blue line) for CN-NV-600; FL spectrum (red line), ECL emission spectrum (black line), and smoothed ECL emission spectrum (blue line) for CN-NV-620; XRD pattern of pristine CN and CN-NV-0.13%, CN-NV-0.42%, CN-NV-0.74%, CN-NV-4.3%, and CN-NV-6.6%; FTIR spectra of pristine CN and CN-NV-0.13%, CN-NV-0.42%, CN-NV-0.74%, CN-NV-4.3%, and CN-NV-6.6%; ESR spectra of pristine CN and CN-NV-0.13%, CN-NV-0.42%, CN-NV-0.74%, CN-NV-4.3%, and CN-NV-6.6%; UV–vis DRS spectra of pristine CN and CN-NV-0.13%, CN-NV-0.42%, CN-NV-0.74%, CN-NV-4.3%, and CN-NV-6.6%; <i>I</i><sub>ECL</sub>–time curves of pristine CN and CN-NVs with different NV contents by KOH-assisted synthesis method-modified GCE in the presence of 0.1 M Na<sub>2</sub>S<sub>2</sub>O<sub>8</sub> range from 0 to −1.5 V (0.1 V/s); normalized FL spectra of pristine CN and CN-NV-0.42%, CN-NV-0.74%, CN-NV-4.3%, and CN-NV-6.6%; normalized smoothed ECL emission spectra of pristine CN and CN-NV-0.42%, CN-NV-0.74%, CN-NV-4.3%, and CN-NV-6.6%; FL spectrum (red line), ECL emission spectrum (black line), and smoothed ECL emission spectrum (blue line) for CN-NV-6.6% (<a class="ext-link" href="/doi/suppl/10.1021/acs.analchem.0c05027/suppl_file/ac0c05027_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, analytical