Abstract:TiO2/SBA-15 catalysts, TiO2 nanoparticles well dispersed on SBA-15 supporter, have been successfully obtained through a self-assembly aging, carboxylation and subsequent solvothermal process. Firstly, P123 (PEG-PPG-PEG), KCl, (2-cyanoethyl) triethoxysilane (CETES) and tetraethoxysilane (TEOS) were employed to form cyano-modified SBA-15 (CN/SBA-15) in 2.0 mol/L HCl solution by Self-assembly aging method. Secondly, carboxyl-modified SBA-15 (COOH/SBA-15) was got through carboxylation treatment in 48% H2SO4 solution at 95 degrees C for 24 h. Finally, highly dispersed TiO2/SBA-15 catalysts were successfully synthesized via solvothermal method at 220 degrees C for 12 h using COOH/SBA-15 and tetrabutyl titanate (TB) as raw materials. In order to remove the organic compounds and improve the crystallization of TiO2, the obtained TiO2/SBA-15 catalysts then were filtrated, washed by absolute ethanol for three times, dried at 80 degrees C and calcined at 550 degrees C for 4 h. Notably, the self-assembly and carboxylation process produced large number of good dispersive carboxyl groups (COOH) on SBA-15, which could effectively anchored TB molecules on SBA-15 to promise the highly dispersion of TiO2 on SBA-15. The obtained TiO2/SBA-15 catalysts have been characterized by X-ray diffraction (XRD), Raman spectrum, Fourier transform infrared spectroscopy (FT-IR), transmission electron microscopy (TEM), nitrogen adsorption and UV-Visible diffuse reflectance spectroscopy (UV-Vis). Above results indicate that the TiO2/SBA-15 catalysts exhibit large specific surface area and TiO2 on SBA-15 supporter is anatase phase, they are both play important roles in photocatalytic application. In the current manuscript, the photocatalytic reduction of CO2 under UV light irradiation as a prober reaction was used to investigate the photocatalytic performance of TiO2/SBA-15 catalysts. It was found that the obtained catalysts performed high photocatalytic capacity for CO2 reduction, especially when the loading amount of TiO2 was around 16.5 wt% [n(COOH)/n(TB)=3], the methanol production got maximum which could reach 80 mu mol/g-catalyst after 6 h UV light irradiation. Compared with the catalysts which synthesized through simple impregnation method, our TiO2/SBA-15 catalysts showed the higher activity in photocatalytic reduction of CO2, owing to the better dispersion and crystallization.

Hierarchical loading of CuO on SiO2 aerogel@high crystalline TiO2 nanofibers for efficiently photocatalytic reduction of CO2 without sacrificial agent

Facile synthesis of hierarchical Ag 3 PO 4 /TiO 2 nanofiber heterostructures with highly enhanced visible light photocatalytic properties

New Insight into Efficient Photocatalytic CO2 Reduction Without Any Sacrifice Agent over the Novel Hierarchical Structured SiOC Whisker Aerogel

New insight into efficient photocatalytic CO 2 reduction without any sacrifice agent over the novel hierarchical structured SiOC whisker aerogel

Modulating Charge Separation of Ce-TiO2 Aerogel Supported on Chitosan Derived Ordered Porous Carbonaceous Frameworks for Promoting CO2 Photoreduction Activity

Coaxial electrospinning prepared Cu species loaded SrTiO3 for efficient photocatalytic reduction of CO2 to CH3OH

Achieving simultaneous Cu particles anchoring in meso-porous TiO2 nanofabrication for enhancing photo-catalytic CO2 reduction through rapid charge separation

Oxygen-vacancy-assisted construction of Ce–TiO2 aerogel for efficiently boosting photocatalytic CO2 reduction without any sacrifice agent

Enhancing photocatalytic CO2 reduction reaction on amorphous Ni@NiO aerogel via oxygen incorporated tuning

Inducing Cu2+ Species to SrTiO3 Nanofibers Based on Blend Electrospinning for Boosting CO2 Photoreduction to CH3OH

Cu2O@Cu@UiO-66-NH2 Ternary Nanocubes for Photocatalytic CO2 Reduction

Cu 2 O@Cu@UiO-66-NH 2 Ternary Nanocubes for Photocatalytic CO 2 Reduction

Synthesis of Supported TiO2/SBA-15 Catalysts and Their Performance on Photocatalytic Reduction of CO2

Ag-Cu Nanoparticles Supported on N-doped TiO2 Nanowire Arrays for Efficient Photocatalytic CO2 Reduction

Fabrication of nano copper oxide evenly patched on cubic sodium tantalate for oriented photocatalytic reduction of carbon dioxide

Molten-salt assisted synthesis of Cu clusters modified TiO2 with oxygen vacancies for efficient photocatalytic reduction of CO2 to CO

Co-embedding oxygen vacancy and copper particles into titanium-based oxides (TiO2, BaTiO3, and SrTiO3) nanoassembly for enhanced CO2 photoreduction through surface/interface synergy

Synchronistic embedding of oxygen vacancy and Ag nanoparticles into potholed TiO 2 nanoparticles-assembly for collaboratively promoting photocatalytic CO 2 reduction

Ordering Bimetallic Cu‐Pd Catalysts onto Orderly Mesoporous SrTiO3‐Crystal Nanotubular Networks for Efficient Carbon Dioxide Photoreduction

Hollow cubic TiO2 loaded with copper and gold nanoparticles for photocatalytic CO2 reduction

Synergistic Effect of Cu2+ and Cu+ in SrTiO3 Nanofibers Promotes the Photocatalytic Reduction of CO2 to Methanol