Abstract:In this study, we develop a facile one-pot approach to the fabrication of poly(L-lactic acid) (PLLA) microsphere-incorporated calcium alginate (ALG-Ca)/hydroxyapatite (HAp) porous scaffolds based on HAp nanoparticle-stabilized oil-in-water Pickering emulsion templates, which contain alginate in the aqueous phase and PLLA in the oil phase. The emulsion aqueous phase is solidified by in situ gelation of alginate with Ca(2+) released from HAp by decreasing pH with slow hydrolysis of D-gluconic acid δ-lactone (GDL) to produce emulsion droplet-incorporated gels, followed by freeze-drying to form porous scaffolds containing microspheres. The pore structure of porous scaffolds can be adjusted by varying the HAp or GDL concentration. The compressive tests show that the increase of HAp or GDL concentration is beneficial to improve the compressive property of porous scaffolds, while the excessive HAp can lead to the decrease in compressive property. Moreover, the swelling behavior studies display that the swelling ratios of porous scaffolds reduce with increasing HAp or GDL concentration. Furthermore, hydrophobic drug ibuprofen (IBU) and hydrophilic drug bovine serum albumin (BSA) are loaded into the microspheres and scaffold matrix, respectively. In vitro drug release results indicate that BSA has a rapid release while IBU has a sustained release in the dual drug-loaded scaffolds. In vitro cell culture experiments verify that mouse bone mesenchymal stem cells can proliferate on the porous scaffolds well, indicating the good biocompatibility of porous scaffolds. All these results demonstrate that the PLLA microsphere-incorporated ALG-Ca/HAp porous scaffolds have a promising potential for tissue engineering and drug delivery applications.

One-step method to construct hydroxyapatite scaffolds with 3-D interconnected structure by a novel hydrogel bead porogen process

A simple hydrogel scaffold with injectability, adhesivity and osteogenic activity for bone regeneration

Novel fabrication of hierarchically porous hydroxyapatite scaffolds with refined porosity and suitable strength

Preparation of 3D Interconnected Macroporous Hydroxyapatite Scaffolds by PVA Assisted Foaming Method

3D PLLA/nano-hydroxyapatite scaffolds with hierarchical porous structure fabricated by low-temperature deposition manufacturing

Preparation and characterization of hydroxyapatite–sodium alginate scaffolds by extrusion freeforming

Biomimetic 3D Hydroxyapatite Architectures with Interconnected Pores Based on Electrospun Biaxially Orientated PCL Nanofibers

Facile Method to Prepare Plga/Hydroxyapatite Composite Scaffold for Bone Tissue Engineering

Fabrication and Biological Application of Nano-Hydroxyapatite (nha)/alginate (alg) Hydrogel As Scaffolds

Fabrication of Poly(lactide‐co‐glycolide) Scaffold Embedded Spatially with Hydroxyapatite Particles on Pore Walls for Bone Tissue Engineering

Alginate/hydroxyapatite hydrogel as biodegradable in situ forming scaffold

Three-dimensional Fully Interconnected Highly Porous Hydroxyapatite Scaffolds Derived from Particle-Stabilized Emulsions

Template-assisted, Sol-gel Fabrication of Biocompatible, Hierarchically Porous Hydroxyapatite Scaffolds

A GelMA-PEGDA-nHA Composite Hydrogel for Bone Tissue Engineering

Rapidly in Situ Forming Biodegradable Hydrogels by Combining Alginate and Hydroxyapatite Nanocrystal

Fabrication and Osteogenesis of a Porous Nanohydroxyapatite/Polyamide Scaffold with an Anisotropic Architecture

Facile Fabrication of Poly(l-Lactic Acid) Microsphere-Incorporated Calcium Alginate/hydroxyapatite Porous Scaffolds Based on Pickering Emulsion Templates

Novel Method to Fabricate Porous N-Ha/pva Hydrogel Scaffolds

Biomimetic Interpenetrating Polymer Network Hydrogels Based on Methacrylated Alginate and Collagen for 3D Pre-Osteoblast Spreading and Osteogenic Differentiation

A novel method for the fabrication of homogeneous hydroxyapatite/collagen nanocomposite and nanocomposite scaffold with hierarchical porosity

Creating hierarchical porosity hydroxyapatite scaffolds with osteoinduction by three-dimensional printing and microwave sintering