Synthesis and characterization of vegetable oil based polyurethane derived from low viscous bio aliphatic isocyanate: Adhesion strength to wood-wood substrate bonding

Swarnalata Sahoo,Hemjyoti Kalita,Smita Mohanty,Sanjay Kumar Nayak

DOI: https://doi.org/10.1007/s13233-017-5080-2

IF: 2.127

2017-05-25

Macromolecular Research

Abstract:In the current study, biobased polyurethane (PU) adhesives at three different stoichiometric ratios of hard (NCO) to soft segment (OH) (1.1:1, 1.3:1, 1.5:1) were prepared by reacting castor oil (CO) based polyol with partially biobased polyisocyanate (PBPI) in the presence of dibutyltin dilaurate (DBTDL) as catalyst. The synthesis of PU adhesive films such as CO-PU1.1:1, CO-PU1.3:1, and CO-PU1.5:1 was confirmed by Fourier transform infrared (FTIR) spectroscopy. The effect of stoichiometric ratios on the bonding strength of wood-to-wood substrate was studied using lap shear strength test. The change in lap shear strength of PU adhesive films subjected to acid and alkali solution was tested. The chemical resistance, surface properties and wetting energies of PU adhesive films were evaluated using scanning electron microscopy (SEM) analysis and contact angle measurement. Thermal stability and activation energy of the films were determined employing thermogravimetric analysis (TGA). The experimental result showed that CO-PU1.3:1 exhibited higher adhesive strength, where as CO-PU1.5:1 exhibited higher thermal stability.