Thermomechanical Performance of Polyester-Based Composites Reinforced with Polypropylene Microfibers and Carbon Black Nanoparticles
Peyman Torkian,Hamid Baseri,Mehdi Karevan
DOI: https://doi.org/10.1007/s11665-024-10335-7
IF: 2.3
2024-11-20
Journal of Materials Engineering and Performance
Abstract:In the present study, composites composed of polyester resin, polypropylene (PP) microfibers, and carbon black (CB) nanoparticles were synthesized, and the effect of filler content (PP microfibers 5, 10, 15, and 20% and CB nanoparticle 1, 5, and 10%) on the mechanical, thermal, structural, and self-healing properties of binary and ternary composites was evaluated. The results of mechanical analysis corroborated that in binary composites, the composite with 10% PP fibers has the highest tensile strength, Young's modulus, flexural strength, and impact strength. Besides, in ternary composites, the composite with 10% PP fibers and 5% CB nanoparticles possessed the maximum impact strength. In this composition, the impact strength increased by 39% compared to the pure resin. X-ray diffraction analysis revealed that the patterns of binary composites were similar to that of pure resin. However, when CB nanoparticles were loaded into the composite, CB crystalline peaks appeared. SEM images verified that the inclusion of 10% PP microfibers leads to the best fiber dispersion and fiber–matrix adhesion, and the increase in microfibers or nanoparticles brings about a decrease in filler dispersion and the appearance of structural defects. Thermal analysis unveiled that the increase in PP fibers does not substantially alter the melting and crystallization of the composites, while the increase in CB nanoparticles gives rise to finer crystals and lower melting points. Contact angle measurement disclosed that in binary composites, the composite with 10% fibers represents the lowest contact angle and, accordingly, the highest wettability. But, in ternary composites, the contact angle did not show a reasonable trend with the filler content. Based on self-healing assay on binary composites, in composites with 15 and 20% PP microfibers, the impact strength, after self-healing, increased by 7 and 9%, respectively.
materials science, multidisciplinary