Abstract:Abstract Monodisperse nanoparticles have attracted great attention in fundamental and applied research. Current protocols for the synthesis of monodisperse nanoparticles typically involve hydrocarbon molecules as surface-capping ligands. Utilizing platinum (Pt)-based nanoparticles for the oxygen reduction reaction (ORR), however, hydrocarbon ligands must be removed in order to expose the surface sites. Here, highly active and durable Pt catalysts are realized without removing the ligands; instead, the native surface ligands are directly converted into uniform, bilayered graphitic shells conformally coated on individual Pt nanoparticles by simple thermal annealing. Strikingly, the annealing temperature is found to be a critical factor dictating the ORR performance of Pt catalysts. Pt nanoparticles thermally treated at 500 oC show a very poor ORR activity, whereas those annealed at 700 oC become highly active along with exceptional stability. In-depth characterization reveals that thermal treatment from 500 to 700 oC triggers the subtle structural reconstruction of carbon shells through graphitization, gradually opening up the porosity without affecting the carbon shell thickness. Additionally, the ligand-derived graphitic shells can effectively prevent Pt nanoparticles from detachment, agglomeration, and dissolution while largely maintaining the accessibility of surface sites. As a result, such graphitic-shell-coated Pt catalysts can exhibit superior long-term stability, largely retaining the activity after 20,000 accelerated durability test cycles in a membrane electrode assembly. Moreover, this ligand carbonization strategy is amenable to Pt-based alloy nanoparticles and can further be extended to modify commercial Pt/C catalysts with substantially enhanced durability. Our work shows that boosting the ORR performance of common Pt nanoparticles is certainly possible by harnessing the native surface ligands, thus offering a robust approach of designing highly durable catalysts for proton-exchange membrane fuel cells.

Highly durable platinum nanoparticles on carbon derived from pitch-based carbon fibers for oxygen reduction reaction

Native ligand carbonization renders common platinum nanoparticles highly durable for electrocatalytic oxygen reduction: annealing temperature matters

Electrochemical Properties of an Atomically Dispersed Platinum Catalyst Formed on a Heat-treated Carbon Support

High activity and durability of carbon-supported core-shell PtP @Pt/C catalyst for oxygen reduction reaction

High Activity and Durability of Carbon-Supported Core-Shell PtPx@Pt/C Catalyst for Oxygen Reduction Reaction

Atomic Platinum Anchored on Fe‐N‐C Material for High Performance Oxygen Reduction Reaction

Synthesis of Platinum Nanocrystals Dispersed on Nitrogen-Doped Hierarchically Porous Carbon with Enhanced Oxygen Reduction Reaction Activity and Durability

Durable carbon-shell-encapsulated Pt/C catalysts synthesized by direct pyrolysis of Pt-pyrrole complexes for the oxygen reduction reaction

Carbon-Capped PtNi Catalysts for the Oxygen Reduction Reaction in Acidic Environment: A Durability Study

Coating Porous TiO2 Films on Carbon Nanotubes to Enhance the Durability of Ultrafine PtCo/CNT Nanocatalysts for the Oxygen Reduction Reaction.

Collaborative Anchoring of Pt Nanoparticles and Metal Oxide Nanoparticles on N-Doped Carbon as Catalysts for Oxygen Reduction

Carbon-coated, methanol-tolerant platinum/graphene catalysts for oxygen reduction reaction with excellent long-term performance

Optimized porous nanostructure of carbon fibers enabling excellent stability of Pt-based catalysts for oxygen reduction reaction

Impact of sp2 carbon material species on Pt nanoparticle-based electrocatalysts produced by one-pot pyrolysis methods with ionic liquids

Conjugated Covalent Organic Frameworks as Platinum Nanoparticle Supports for Catalyzing the Oxygen Reduction Reaction

Activity and Durability of Platinum-Based Electrocatalysts Supported on Bare or Fluorinated Nanostructured Carbon Substrates

Immobilization of Platinum Nanoparticles on Covalent Organic Framework‐Derived Carbon for Oxygen Reduction Catalysis

High‐Temperature Confinement Synthesis of Supported Pt–Ni Nanoparticles for Efficiently Catalyzing Oxygen Reduction Reaction

An elegant 3D-ordered hierarchically porous framework to anchor Pt nanocrystals for durable oxygen reduction reaction

Carbon material loaded with platinum and iron oxide nanoparticles as a low-platinum catalyst for oxygen reduction reaction