Preparing water-soluble 2, 3-dialdehyde cellulose as a bio-origin cross-linker of chitosan

Xiuzhi Tian,Xue Jiang

DOI: https://doi.org/10.1007/s10570-017-1607-0

IF: 6.123

2017-12-29

Cellulose

Abstract:AbstractDialdehyde celluloses (DACs) with smaller nanocrystals were prepared during the oxidization of nanocrystalline cellulose (NCC) using increased NaIO4. When NCC from the hydrolysis of microcrystalline cellulose (64 wt% H2SO4, 45 °C, 1 h) was periodate oxidized at NaIO4/anhydroglucose unit mole ratio of 5 and pH 6.5 for 5 h, the product of DAC5 can easily dissolve in water at ambient temperature. It was adopted as a bio-origin cross-linker of chitosan (CTS). The CTS films cross-linked with 1 ~ 7% DAC5 (relative to the weight of CTS in the dried film) were fabricated by the solution casting technique. FT-IR, XRD and SEM characterizations demonstrated the cross-linking reaction of DAC5 with CTS and the good compatibility between them. The dissolving and mechanical testing results showed that the cross-linked film had improved acid resistance and tensile strength compared to the pure CTS film. They could be applied in the areas of food packaging and biomedical treatments.

materials science, textiles,polymer science, paper & wood