The Role of Silanization of Barium Strontium Titanate Nanopowders on the Dielectric Constant and Thermal Stability of Epoxy Nanocomposites
Ngoc Chau Chu,Thi Tuyet Mai Phan,Duc Trung Bui,Hoan Nguyen Xuan,Pascal Carriere
DOI: https://doi.org/10.1002/slct.202403061
2024-10-02
ChemistrySelect
Abstract:The (Ba0.95,Sr0.05)TiO3/epoxy nanocomposite were prepared using the bar‐coating technique. Adding γ‐APS silane functional nano‐(Ba,Sr)TiO3 with a finely tuned interface plays a crucial role in significantly increasing the glass transition temperature and exhibiting good thermal stability. The dielectric constant improved by ~1.5 times compared to the neat epoxy resins and the nanocomposite incorporating (Ba,Sr)TiO3 non‐modified silane sample. This paper reports polymer composites′ microstructure and dielectric properties based on an epoxy resin matrix containing different amounts (from 2–10 wt. %) of barium strontium titanate nanoparticles. (Ba,Sr)TiO3 was prepared using the hydrothermal method, showing an average particle size of 100 nm. The composites′ thermal properties and morphology were characterized using thermogravimetric analysis, differential scanning calorimetry, and scanning electron microscopy. Our studies show that the (Ba,Sr)TiO3 nanoparticles were well dispersed in the epoxy resin matrix thanks to controlled silane functionalization. Accordingly, the glass transition temperature (Tg) value of the nanocomposites was found to be 159.0 °C at 10 wt. % (Ba,Sr)TiO3 loading and is higher than the neat epoxy resin Tg (Tg=154.7 °C). Moreover, the dielectric composite properties were investigated comprehensively via a wide range of frequencies from 10 Hz to 100 kHz. The results indicate that (Ba,Sr)TiO3 nanopowders and the surface modifying filler play a crucial role in the significant increase of the dielectric constants, approximately 1.5 times at the optimum added amount (Ba,Sr)TiO3. The limited functionalization of (Ba,Sr)TiO3 nanoparticles by the silane affords to control the nanocomposite dielectric loss. Furthermore, the nanocomposites also exhibited good thermal stability.
chemistry, multidisciplinary