Abstract:In the industry, chrome coating is an important player in the functional layer application. Due to its high corrosion and wear resistance as well as high hardness [1], hard chrome plating is a popular choice in the automotive and aerospace industry. However, since September 2017, the application of chrome (VI) in surface treatment is banned by the European Chemical Agency (ECHA) due to chrome (VI) being toxic and environmentally hazardous [2]. Chrome (III) compound is a popular substitute for chrome (VI) due to it being less toxic compared to chrome (VI). However, chrome (III) coating has a lower corrosion resistance, and the electroplating process is more sensitive to metallic impurities. Many new innovations have since been developed such as the plasma electrolytic oxidation (PEO), extreme highspeed laser deposition (EHLA). Even established technologies such as physical vapour deposition (PVD), thermal spraying and case hardening process have tried to replace hard chrome coating with a degree of success. Admittedly, the above-mentioned technologies have their fair share of disadvantages. PEO, a green procedure [3], causes a metal substrate to develop a highly resistant oxide which is extremely strong and corrosion as well as wear resistant. The process however needs a high temperature and pressure, continuous replacement of electrolytes and consumes a great amount of power which made the process not feasible for a wide industrial application [4-6]. EHLA and thermal spraying on the other hand are restricted to rotational symmetric components. PVD is restricted to substrates that can handle high processing temperature like nitrable ferrous base materials. Lastly, case hardening processes requires long heat treatments which contribute to a higher process cost. [7] In our presentation, another alternative for chrome coating based on electrodeposition will be introduced. The element tungsten is considered in our experiments because tungsten not only has an excellent corrosion properties and high tensile strength at high temperature, but it also has a microhardness of 650 Vickers. However, it is not possible to deposit tungsten from an aqueous solution because tungstate cannot be directly reduced to metallic tungsten due to a very low overvoltage for hydrogen evolution on tungsten. Thus, an induced co-deposition mechanism is needed, and it is known that tungsten can be easily codeposited with iron group metal. [8-9] In this study a modified Watt's bath is used as electrolyte to deposit NiW alloy. Our preliminary tests have shown that tungsten can also be deposited with nickel without the help of citric acid as complexing agent. The usage of citric acid does indeed inhibit the deposition of nickel but show no influence in the deposition of tungsten. Hence, in our study, experiments with the rotating disc electrode (RDE) will be done to see if tungsten content in the coating could be increased when the hydrodynamic and coating parameters are manipulated. The chemical composition of the layer is measured using SEM/EDX and the surface morphology is pictured using SEM. Metallographic cross-sections are made to see if there are any fissures in the layer and the hardness of the layer is measured using the microhardness test. The dependency of hardness on the tungsten content in the layer and the annealing parameter will also be shown in the presentation. XRD measurement is conducted for phase analysis and grain size calculation. Figure 1

Effect of Electrochemical Bath Composition on the Preparation of Ni-W-Fe-P Amorphous Alloy

Preparation and Properties of Textured Ni–W Coatings Electrodeposited on the Steel Surface from a Pyrophosphate Bath

Electrodeposition of Ni-W Alloy in Sulphate System

Study on Electroless Plating Ni-W-P Ternary Alloy with High Tungsten from Compound Complexant Bath

Electrodeposition of Ni-W-P alloy

Effect of Tungsten on Microstructures of Annealed Electrodeposited Ni-W Alloy and Its Corrosion Resistance

Optimization of the Electroplating Process for Amorphous Nickel- Phosphorus Alloy

The Effects of Na2WO4 Concentration on the Properties of Microarc Oxidation Coatings on Aluminum Alloy

The Effect of Tungsten Additive on the Surface Characteristics of Amorphous Ni–P Alloy

Influence of the bath pH value on the microstructure and properties of a novel electrodeposited Ni-W-Ti3C2TX composite coating

Effect of electroless deposition on the corrosion resistance property for NdFeB permanent magnets with surface coating of Ni-P alloy

Electrodeposition of nanocrystalline Ni-W coatings with citric acid system

Influences of Co and process parameters on structure and corrosion properties of nanocrystalline Ni-W-Co ternary alloy film fabricated by electrodeposition at low current density

Preparation of Amorphous Nickel-Phosphorus Alloy Coating by Electroplating

Influence of Positional Isomeric Spacers of Naphthalene Derivatives on Ni–W Alloy Electrodeposition: Electrochemical and Microstructural Properties

Electrodeposition of Ni-W Alloy from Citric Acid Free Aqueous Electrolyte As a Substitute for Hard Chrome Coating and the Effect of Tungsten Content on Coating Hardness

ZINC-NICKEL ALLOY ELECTROPLATING IN AN ALKALINE BATH

Synthesis, Composition, Morphology, and Wettability of Electroless Ni-Fe-P Coatings with Varying Microstructures

Preparation, characterisation and electrochemical study of crack-free nanocrystalline electrodeposited Co-W alloy coating of high hardness

Electrodeposition of High Entropy Alloy of Ni-Co-Cu-Mo-W from an Aqueous Bath

Study of Electroless Ni-Zn-P Alloy Plating from Acidic Bath