Abstract:Light-driven 3D printing to convert liquid resins into solid objects (i.e., photocuring) has traditionally been dominated by engineering disciplines, yielding the fastest build speeds and highest resolution of any additive manufacturing process. However, the reliance on high-energy UV/violet light limits the materials scope due to degradation and attenuation (e.g., absorption and/or scattering). Chemical innovation to shift the spectrum into more mild and tunable visible wavelengths promises to improve compatibility and expand the repertoire of accessible objects, including those containing biological compounds, nanocomposites, and multimaterial structures. Photochemistry at these longer wavelengths currently suffers from slow reaction times precluding its utility. Herein, novel panchromatic photopolymer resins were developed and applied for the first time to realize rapid high-resolution visible light 3D printing. The combination of electron-deficient and electron-rich coinitiators was critical to overcoming the speed-limited photocuring with visible light. Furthermore, azo-dyes were identified as vital resin components to confine curing to irradiation zones, improving spatial resolution. A unique screening method was used to streamline optimization (e.g., exposure time and azo-dye loading) and correlate resin composition to resolution, cure rate, and mechanical performance. Ultimately, a versatile and general visible-light-based printing method was shown to afford (1) stiff and soft objects with feature sizes <100 μm, (2) build speeds up to 45 mm/h, and (3) mechanical isotropy, rivaling modern UV-based 3D printing technology and providing a foundation from which bio- and composite-printing can emerge.Liquid resins that rapidly harden upon exposure to low-energy visible light are developed and applied to high-resolution projection-based 3D printing across the color spectrum.This article has not yet been cited by other publications.

High-resolution 3D photopolymerization assisted by upconversion nanoparticles for rapid prototyping applications

High-resolution 3D Nanoprinting Based on Two-Step Absorption Via an Integrated Fiber-Coupled Laser Diode.

Beyond 100 nm Resolution in 3D Laser Lithography: Post Processing Solutions

Heterostructured Photoinitiator Comprising Upconversion Particles and Metal–Organic Frameworks for Enhanced Near-Infrared Photopolymerization: Implications for 3D Printing

Multi-photon polymerization using upconversion nanoparticles for tunable feature-size printing

Upconversion 3D printing enables single-immersion multi-material stereolithography

Photothermal synergy mechanism in near-infrared photopolymerization for 3D printing acceleration and mechanical enhancement

Rapid High-Resolution Visible Light 3D Printing

Photocurable High-Energy Polymer-Based Materials for 3D Printing

Molded Transparent Photopolymers and Phase Shift Optics for Fabricating Three Dimensional Nanostructures.

Visible‐Light‐Driven Rapid 3D Printing of Photoresponsive Resins for Optically Clear Multifunctional 3D Objects (Adv. Mater. 19/2024)

Near-Infrared Light Driven Photopolymerization Based On Photon Upconversion

3D Printing of Resin Composites Doped with Upconversion Nanoparticles for Anti-Counterfeiting and Temperature Detection.

Role of energy transfer in a nanoinitiator complex for upconversion- driven polymerization

Photoinduced Free Radical Promoted Cationic RAFT Polymerization Toward "living" 3D Printing.

Micro 3D Printing by Two-Photon Polymerization: Configurations and Parameters for the Nanoscribe System

Extremely deep photopolymerization using upconversion particles as internal lamps

Triplet Fusion Upconversion Nanocapsules for Volumetric 3D Printing

Refractive index matched polymeric and preceramic resins for height-scalable two-photon lithography

Multiphoton-excited DUV photolithography for 3D nanofabrication

Customizable and Reconfigurable Surface Properties of Printed Micro‐objects by 3D Direct Laser Writing via Nitroxide Mediated Photopolymerization