Abstract:Thermal and simultaneous thermal and gamma radiation aging experiments were conducted on an industry grade cross-linked polyethylene (XLPE) cable insulation material, which is a composite material with XLPE as polymer matrix and various additives and fillers. Reverse engineering was conducted to identify and quantify the material composition given that this information was not revealed by the cable manufacture. Samples were then aged at temperatures of 60, 90, and 115 °C, exposed to gamma radiation for total doses of 0 to 324 kGy, and at dose rates of 0 to 540 Gy/h. Aging mechanisms were studied using various materials characterization techniques including pyrolysis gas chromatography mass spectrometry (Py-GCMS), differential scanning calorimetry (DSC), nuclear magnetic resonance spectroscopy (NMR), and gel-fraction tests. Results show that the flame-retardant components were decomposed into smaller molecules when the material was exposed to gamma radiation, while no changes were observed when the samples were aged thermally without gamma radiation. With exposure to gamma radiation, the crystalline phase of the XLPE were damaged by gamma radiation introducing defects in the crystals, resulting in smaller and less perfect crystals. The dominance of chain scission or chain reformation process largely depends on the chain mobility, which is decided by the aging temperature. Chain scission was seen to dominate when the material was exposed to gamma radiation at 60 °C. Chain cross-linking slightly dominated when the material was exposed to gamma radiation at 90 °C and became more dominant with exposure to gamma radiation at 115 °C. No significant change to the XLPE polymer matrix was observed when the samples were exposed to thermal aging without gamma radiation. Antioxidant is more effective in protecting the XLPE polymer matrix under thermal aging, but less effective with sample exposure to gamma radiation.

Effect of gamma irradiation on titanium dioxide-filled polymer composites in cable insulation applications

Effect of Gamma-Ray Irradiation on Dielectric Properties of PP/Elastomer/TiO2 Nanocomposite

The Effects of Irradiation Cross-Linking on the Thermal Degradation and Flame-Retardant Properties of the Hdpe/Eva/Magnesium Hydroxide Composites

Effect of Gamma-Ray Irradiation on Dielectric Properties of Polypropylene As Cable Insulation

Effects of Electron Beam Irradiation on the Mechanical, Thermal, and Surface Properties of Some EPDM/Butyl Rubber Composites

Aging Behavior of Polypropylene As Cable Insulation under Gamma-Ray Irradiation

Effect of Irradiation Dose Rates on Ethylene-Propylene Rubber for Nuclear Cables

Effect of Radiation Vulcanization on the Mechanical Properties of Ethylene Propylene Dine Terpolymer Rubber

Effect of Antioxidant on Irradiation Resistance of PP Composites for Nuclear Cable Insulation

Improvement of electrical insulation performance of silicone rubber cables due to exposure to heat and radiation

PVC nanocomposites for cable insulation with enhanced dielectric properties, partial discharge resistance and mechanical performance

Tailoring Electrical Properties of PVC/PEC/Co 3 O 4 Nanocomposites by Electron Beam Irradiation for Advanced Medium Voltage Cable Applications

Effects of γ irradiation on the structure, physical and mechanical properties of a series of tetrafunctional epoxies modified DGEBA/DDS

A comparative study of the mechanical and thermal properties of EPDM rubber/cement kiln dust composite cured by ionizing radiation

Degradation mechanisms of cable insulation materials during radiation–thermal ageing in radiation environment

Physicochemical properties and flame retardancy of irradiated EPDM nanocomposites and possible application as insulating materials

Radiation Degradation of Polytetrafluoroethylene-Lead Composites

Aging mechanisms of filled cross-linked polyethylene (XLPE) cable insulation material exposed to simultaneous thermal and gamma radiation

Gamma irradiation-induced degradation of silicone encapsulation

Gamma radiation effects on polydimethylsiloxane in hydrogen peroxide solution

Gamma Irradiation Effect on Polymeric Chains of Epoxy Adhesive