Assisted Tip Sonication Approach for Graphene Synthesis in Aqueous Dispersion

Ahmed F Ghanem,Mona H Abdel Rehim,Ahmed Ghanem,Mona Abdel Rehim
DOI: https://doi.org/10.3390/biomedicines6020063
IF: 4.757
2018-05-28
Biomedicines
Abstract:Graphene (G) is a newcomer material that holds promising properties for many applications. The production of high quality G with a good yield is a long-standing goal for many researchers. This work emphasizes synthesis of dispersed graphene nanoplatelets (DGP) through aqueous dispersion technique in surfactant/water solution with the aid of tip sonication. A chemical method was also used to prepare graphene oxide (GO) and reduced graphene oxide (RGO) for comparison. Elemental analysis revealed the C:O ratio to be 12:1 for DGP but much lower for other graphene structures. Optical characterization of DGP, GO and RGO with UV and Raman spectroscopy confirmed the ideal structure of DGP. Moreover, X-ray diffraction (XRD) revealed the amorphous structure of DGP. Transmission electron microscope (TEM) imaging showed that DGP was composed of a few flat layers, unlike the wrinkled and partially bent multilayered G. Topological study of the DGP surface with scanning electron microscope (SEM) depicted its rough surface with (r<sub>a</sub>) value of 35 nm, as revealed using an atomic force microscope (AFM). Electrochemical measurements confirmed the higher conductivity of DGP over graphene prepared by chemical method due to lack of structural defects. Its perfect structure facilitates the mobility of charge carriers that makes it preferable in optoelectronic applications.
biochemistry & molecular biology,medicine, research & experimental,pharmacology & pharmacy
What problem does this paper attempt to address?
The main problem this paper attempts to address is the synthesis of high-quality dispersed graphene nanoplatelets (DGP) through aqueous phase dispersion technology combined with probe ultrasonication. Specifically, the authors aim to overcome the drawbacks of traditional chemical methods for graphene preparation, such as structural defects and low electrical conductivity, and to explore an environmentally friendly and efficient method for graphene preparation. ### Background and Objectives of the Paper 1. **Properties and Applications of Graphene**: - Graphene is a two-dimensional carbon material with excellent thermal and electrical properties and extremely high mechanical strength. - Graphene has wide applications in sensors, gas and energy storage, optoelectronics, polymer composites, and catalysis. 2. **Problems with Existing Preparation Methods**: - Chemical vapor deposition (CVD) and molecular building block methods can produce high-quality graphene, but the yield is limited. - Chemical methods (such as the Hummer method) can produce graphene on a large scale, but the resulting graphene has structural defects that affect its electrical conductivity. - Liquid phase exfoliation is a promising preparation method but requires the use of toxic solvents or complex surfactants. 3. **Research Objectives**: - Develop an environmentally friendly and efficient method for graphene preparation by synthesizing high-quality dispersed graphene nanoplatelets (DGP) through aqueous phase dispersion technology and probe ultrasonication. - Verify the structure and performance of DGP, particularly its electrical conductivity and surface characteristics. ### Experimental Methods 1. **Materials**: - Graphite powder, sodium dodecylbenzene sulfonate (SDS), sulfuric acid, and other reagents were used. 2. **Synthesis Methods**: - **Reduced Graphene Oxide (RGO)**: The Hummer method was used, including oxidation and reduction steps. - **Dispersed Graphene Nanoplatelets (DGP)**: Graphite powder and SDS were mixed and then subjected to ultrasonication, followed by centrifugation to obtain DGP. 3. **Characterization Methods**: - **Scanning Electron Microscopy (SEM)**: To observe the morphology of the samples. - **Elemental Analysis**: To determine the content of carbon and other elements in the samples. - **Raman Spectroscopy**: To analyze the structure and defects of the samples. - **X-ray Diffraction (XRD)**: To study the crystal structure of the samples. - **Transmission Electron Microscopy (TEM)**: To observe the microstructure of the samples. - **Atomic Force Microscopy (AFM)**: To measure the surface roughness of the samples. - **Electrochemical Testing**: To evaluate the electrical conductivity of the samples. ### Results and Discussion 1. **Elemental Analysis**: - The carbon to oxygen ratio of DGP is 12:1, much higher than that of RGO (2.6:1), indicating that DGP has fewer oxygen-containing functional groups and a more complete structure. 2. **Raman Spectroscopy**: - The intensity ratio of the D band to the G band (I_D/I_G) for DGP is 0.39, much lower than that of RGO (1.17) and GO (1.08), indicating fewer structural defects in DGP. - The intensity of the 2D band is relatively low, indicating that DGP consists of multiple layers of graphene. 3. **Electrochemical Performance**: - The electrical conductivity of DGP is significantly higher than that of RGO, attributed to fewer structural defects and higher charge carrier mobility. ### Conclusion This study successfully developed an environmentally friendly and efficient aqueous phase dispersion technology combined with probe ultrasonication to synthesize high-quality dispersed graphene nanoplatelets (DGP). DGP has fewer structural defects and higher electrical conductivity, making it suitable for applications in optoelectronics and other fields.