Workability and Crack Recovery Performance Investigation of IPDI Microcapsules–Based Self-Healing Cement Paste
Sun Dawei,Ma Wenxu,Ma Jikun,Mao Qianjin,Lan Mingzhang,Wang Ziming,Sun Shibing,Tian Yingliang,Guo Hongxia,Cui Suping,Sun Dawei; Ma Wenxu; Ma Jikun; Mao Qianjin; Lan Mingzhang; Wang Ziming; Sun Shibing; Tian Yingliang; Guo Hongxia; and Cui Suping1Lecturer,College of Materials Science and Engineering,Beijing Univ. of Technology,Beijing 100124,China (corresponding author). ORCID: https://orcid.org/0000-0003-4703-4737. Email: 2College of Materials Science and Engineering,Beijing Univ. of Technology,Beijing 100124,China. Email: mawx@emails.bjut.edu.cn3College of Materials Science and Engineering,Beijing Univ. of Technology,Beijing 100124,China. Email: 871607505@qq.com4Professor,College of Materials Science and Engineering,Beijing Univ. of Technology,Beijing 100124,China. Email: maoqj@bjut.edu.cn5Professor,College of Materials Science and Engineering,Beijing Univ. of Technology,Beijing 100124,China. Email: lanmingzhang@bjut.edu.cn6Professor,College of Materials Science and Engineering,Beijing Univ. of Technology,Beijing 100124,China. Email: wangziming@bjut.edu.cn7Professor,College of Materials Science and Engineering,Beijing Univ. of Technology,Beijing 100124,China. Email: sunshibing@bjut.edu.cn8Professor,College of Materials Science and Engineering,Beijing Univ. of Technology,Beijing 100124,China. Email: tianyl@bjut.edu.cn9Professor,College of Materials Science and Engineering,Beijing Univ. of Technology,Beijing 100124,China. Email: hxguo@bjut.edu.cn10Professor,College of Materials Science and Engineering,Beijing Univ. of Technology,Beijing 100124,China. Email: cuisuping@bjut.edu.cn
DOI: https://doi.org/10.1061/(asce)mt.1943-5533.0003768
IF: 3.2
2021-04-29
Journal of Materials in Civil Engineering
Abstract:Isophorone diisocyanate (IPDI) was encapsulated successfully within double-layered shells, and final microcapsules showed outstanding self-healing functions in cement paste. The well-dispersed microcapsules had a diameter of 347.0±103.4 μm , shell thickness of 3.1±0.4 μm , and core fraction around 74.8%±1.9% by weight. The diameters of microcapsules were adjustable by varying agitation rates. The beginning weight-loss temperature of microcapsules was 200°C, implying good thermal stability. The final microcapsules affected slightly the workability and setting time of fresh self-healing cement paste. Although the mechanical strength of hardened self-healing cement paste was decreased with the increase of microcapsule concentrations, the open porosity was improved obviously from 33.5% (control samples) to 31.8% when 5.0% by weight of microcapsules was introduced. The interfaces of microcapsules were compatible enough with cement paste without obvious delamination. Especially, the self-healing cement paste showed outstanding self-healing functions in open air when 10.0% by weight of microcapsules was introduced.
construction & building technology,materials science, multidisciplinary,engineering, civil