Abstract:With increasing demand of green and inexpensive power source with long cycle life and high power density, supercapacitors based on biomass-based active carbons have attracted wide attention in recent years. However, the electrochemical performances of the biomass-based active carbons are still not competitive and the control of their mi-crostructure still remains a challenge. Therefore, waste biomass furfural residue is employed as raw material to prepare porous carbon for supercapacitors. The waste biomass-based porous carbon with obviously improved electrochemical performance was prepared by two-step carbonization process under the protection of argon by using KOH as activated agent. The morphology, structure and composition of final porous carbon materials were characterized by SEM, TEM, Raman, XPS, XRD, etc. The effect of different KOH/precursor weight ratio on the textural properties and sur-face chemistry of KOH-activated carbons was examined. The results showed that the natural hierarchical structure of furfural residue can be preserved and the furfural residue based porous carbon materials ( FRC ) have 3D interconnected porous structure, and the sample synthesized at 3∶1 ratio of KOH and furfural residue, under 750 ℃has the highest BET surface area of 2 164.3 m2/g. When applied as the electrode material of supercapacitor device, the FRC exhibits outstanding capacitive performance with specific capacitance of 298 F/g at 0.5 A/g, good rate ca-pacitive behavior, and excellent cycling stability (97% of capacitance retention after 10 000 cycles) in 6 mol/L KOH electrolyte. The specific energy density of the device is about 8.18 W/(h·kg) at a current density of 0.5 A/g. And the specific energy density is still 4.58 W/(h·kg) with a high power density of 3 750 W/kg, which is superior to that of the commercial devices based on two symmetric activated carbon electrodes. These porous carbons derived from low-cost waste biomass are expected to be ideal electrode material for supercapacitors. The present approach represents a sustainable platform towards the rational design of carbon materials and the efficient utilization of biomass resources.

A facile approach to prepare biomass-derived activated carbon hollow fibers from wood waste as high-performance supercapacitor electrodes

Porous carbon derived from cashew nut husk biomass waste for high-performance supercapacitors

Sawdust-Derived Activated Carbon with Hierarchical Pores for High-Performance Symmetric Supercapacitors

Wood-derived Biochar As Thick Electrodes for High-Rate Performance Supercapacitors

Acid-modified biomass-based N-doped O-rich hierarchical porous carbon as a high-performance electrode for supercapacitors

Novel Synthesis Route for the Preparation of Mesoporous Nitrogen-Doped Carbons from Forestry Wastes for Supercapacitors

Peanut shell waste derived porous carbon for high-performance supercapacitors

Ultrahigh yield of nitrogen doped porous carbon from biomass waste for supercapacitor

High performance flexible supercapacitors based on porous wood carbon slices derived from Chinese fir wood scraps

Preparation of porous carbons from furfural residue and its application to high-performance supercapacitors

Biobased Nano Porous Active Carbon Fibers for High-Performance Supercapacitors

Biological treatment as a green approach for enhancing electrochemical performance of wood derived carbon based supercapacitor electrodes

High-mass loaded redox-active lignin functionalized carbonized wood collector to construct sustainable and high-performance supercapacitors

Polypyrrole-decorated hierarchical carbon aerogel from liquefied wood enabling high energy density and capacitance supercapacitor

Nitrogen enriched high specific surface area biomass porous carbon: A promising electrode material for supercapacitors

High performance supercapacitors based on wood-derived thick carbon electrodes synthesized via green activation process

Fabrication of Biomass-Derived Activated Carbon with Interconnected Hierarchical Architecture Via H3PO4-assisted KOH Activation for High-Performance Symmetrical Supercapacitors

Foaming waste wine yeast mud into nitrogen doped porous carbon framework by recyclable activator for high specific energy supercapacitor

High-performance N-doped activated carbon derived from walnut green peel for supercapacitors

Durian shell-derived N, O, P-doped activated porous carbon materials and their electrochemical performance in supercapacitor

Porous carbon from verbena straw with self-doped O/N and its high-performance aqueous and flexible all-solid-state supercapacitors