Abstract:Polyether-ether-ketone (PEEK) is increasingly becoming popular in medicine because of its excellent mechanical strength, dimensional stability, and chemical resistance properties. However, PEEK being bioinert, has weak bone osseointegration properties, limiting its clinical applications. In this study, a porous PEEK structure was developed using a chemical etching method with 98 wt% sulfuric acids and three post-treatments were performed to improve bone cell adhesion and proliferation. Four groups of PEEK samples were prepared for the study: Control (untreated; Group 1); Etched with sulfuric acid and washed with distilled water (Group 2); Etched with sulfuric acid and washed with acetone and distilled water (Group 3); and Etched with sulfuric acid and washed with 4 wt% sodium hydroxide and distilled water (Group 4). Surface characterization of the different groups was evaluated for surface topology, porosity, roughness, and wettability using various techniques, including scanning electron microscopy, profilometer, and goniometer. Further chemical characterization was done using Energy-dispersive X-ray spectroscopy to analyze the elements on the surface of each group. Bone cell studies were conducted using cell toxicity and alkaline phosphatase activity (ALP) assays. The SEM analysis of the different groups revealed porous structures in the treatment groups, while the control group showed a flat topology. There was no statistically significant difference between the pore size within the treated groups. This was further confirmed by the roughness values measured with the profilometer. We found a statistically significant increase in the roughness from 7.22 × 10 −3 μm for the control group to the roughness range of 0.1 μm for the treated groups (Groups 2–4). EDX analysis revealed the presence of a 0.1% weight concentration of sodium on the surface of Group 4, while sulfur weight percentage concentration was 1.1%, 0.1%, and 1.4% in groups 2, 3, and 4, respectively, indicating different surface chemistry on the surface due to different post-treatments. Cell toxicity decreased, and ALP activity increased in groups 3 and 4 over 7 days compared with the control group. It is demonstrated that the surface modification of PEEK using a chemical etching method with post-processing with either acetone or sodium hydroxide provides a nano-porous structure with improved properties, leading to enhanced osteoblastic cell differentiation and osteogenic potential.

Production and sulfonation of bioactive polyetheretherketone foam for bone substitute applications

Influence of Sulfur Content on Bone Formation and Antibacterial Ability of Sulfonated PEEK.

PEEK surface modification by fast ambient-temperature sulfonation for bone implant applications

Surface modification of Polyether-ether-ketone for enhanced cell response: a chemical etching approach

Gaseous Sulfur Trioxide Induced Controllable Sulfonation Promoting Biomineralization and Osseointegration of Polyetheretherketone Implants

Additive manufacturing and in vitro study of biological characteristics of sulfonated polyetheretherketone-bioactive glass porous bone scaffolds

Effect of Surface Modification of PEEK Artificial Phalanx by 3D Printing on its Biological Activity

Surface Phosphonation Treatment Shows Dose-Dependent Enhancement of the Bioactivity of Polyetheretherketone

Effects of different sulfonation times and post-treatment methods on the characterization and cytocompatibility of sulfonated PEEK

Enhanced Osteogenic Activities of Polyetheretherketone Surface Modified by Poly(sodium P‐styrene Sulfonate) Via Ultraviolet‐induced Polymerization

Enhancing bioactivity and biocompatibility of polyetheretherketone (PEEK) for dental and maxillofacial implants: A novel sequential soaking process

Surface bioactivation of Polyetheretherketone (PEEK) by magnesium chondroitin sulfate (MgCS) as orthopedic implants for reconstruction of skeletal defects

Plasma Surface Functionalized Polyetheretherketone for Enhanced Osseo-Integration at Bone-Implant Interface

Micro-porous polyetheretherketone implants decorated with BMP-2 via phosphorylated gelatin coating for enhancing cell adhesion and osteogenic differentiation.

The sulfonated polyetheretherketone with 3D structure modified by two bio-inspired methods shows osteogenic and antibacterial functions

Surface modification of polyether ether ketone implant with a novel nanocomposite coating containing poly (vinylidene fluoride) toward improving piezoelectric and bioactivity performance

Polyetheretherketone Surface Engineered with a Degradable Hybrid Coating for Accelerating Osteogenesis

Additively-manufactured Poly-Ether-ether-ketone (PEEK) Lattice Scaffolds with Uniform Microporous Architectures for Enhanced Cellular Response and Soft Tissue Adhesion

Surface Modification of Poly(ether ether ketone) by Simple Chemical Grafting of Strontium Chondroitin Sulfate to Improve its Anti‐inflammation, Angiogenesis, Osteogenic Properties

Surface porous poly-ether-ether-ketone based on three-dimensional printing for load-bearing orthopedic implant

Surface phosphonation treatment shows dose-dependent enhancement of the bioactivity of polyetheretherketone (vol 9, pg 30076, 2019)