Structural characterization and antibacterial activity of hydroxyapatite synthesized via sol-gel method using glutinous rice as a template

P. Phatai,C. M. Futalan,S. Kamonwannasit,P. Khemthong

DOI: https://doi.org/10.1007/s10971-018-4910-9

2019-01-05

Abstract:<h3 class="a-plus-plus">Abstract</h3> <p class="a-plus-plus">The present work aims to synthesize hydroxyapatite (HAp) via green template addition using glutinous rice (GR) in combination with sol-gel route under various calcination temperatures (500–900 °C). The physicochemical properties of GR-HAp were analyzed using X-ray diffraction, Fourier-transform infrared spectroscopy, scanning electron microscopy, transmission electron microscopy, and energy dispersive X-ray analysis. The utilization of GR as template in HAp synthesis resulted in the formation of GR-HAp particles that are less crystalline. Surface morphology revealed discrete, rod-shaped GR-HAp particles were formed at low calcination temperature (500–600 °C), while larger particles were formed as temperature was increased. Results confirmed that higher calcination temperature led to the transformation of HAp into various phases including β-Ca<sub class="a-plus-plus">3</sub>(PO<sub class="a-plus-plus">4</sub>)<sub class="a-plus-plus">2</sub>, CaO, and β-NaCa(PO<sub class="a-plus-plus">4</sub>). In addition, the formation of smaller, elongated GR-HAp particles with diameter of 75–180 nm and homogenous particle size distribution was attained at 900 °C. The antibacterial activity was evaluated via disc diffusion method against four Gram-positive bacteria including <em class="a-plus-plus">B. cereus</em>, <em class="a-plus-plus">B. subtilis</em>, <em class="a-plus-plus">S. aureus</em>, and <em class="a-plus-plus">S. epidermidis</em>, and two Gram-negative bacteria including <em class="a-plus-plus">E. coli</em> and <em class="a-plus-plus">P. aeruginosa</em>. The GR-HAp powder calcined at 900 °C showed strong antibacterial performance against all bacterial strains with inhibition zones ranging from 11.66–16.66 mm, which indicates its suitability to be utilized as a material in biomedical applications.<span class="a-plus-plus figure category-standard float-no id-figa"> <span class="a-plus-plus media-object"> <img alt="" src="https://static-content.springer.com/image/MediaObjects/10971_2018_4910_Figa_HTML.png" class="a-plus-plus"/> </span> </span></p>

materials science, ceramics