Covalently connected core–shell NH2-UiO-66@Br-COFs hybrid materials for CO2 capture and I2 vapor adsorption

Jiajia Wang,Lizhi Wang,You Wang,Fan Yang,Jiawei Li,Xiyuan Guan,Junjiang Zong,Fa Zhou,Jianhan Huang,You-Nian Liu

DOI: https://doi.org/10.1016/j.cej.2022.135555

IF: 15.1

2022-06-01

Chemical Engineering Journal

Abstract:Metal organic frameworks (MOFs)@covalent organic frameworks (COFs) (MOFs@COFs) hybrid materials not only combine the advantages of MOFs and COFs, but the possible synergistic effect at the MOFs-COFs interface can improve the performance of the hybrid materials greatly. Herein, the Br-COFs shell was in-situ grown on the surface of the NH2-UiO-66 core by Schiff-based reaction and a kind of novel covalently connected core–shell NH2-UiO-66@Br-COFs hybrid materials were prepared accordingly. Unique structure was generated at the core–shell interface which could be effectively adjusted by the coating amount of Br-COFs. In particular, abundant ultramicropores were generated at the interfacial layers as compared with NH2-UiO-66 and Br-COFs, and the maximum ultramicropore volume (V ultra) was up to 0.157 cm3·g−1. These produced ultramicropores at the core–shell interface made a great positive contribution to the CO2 capacity and the maximum CO2 capacity of the hybrid materials was measured to be 169.5 mg·g−1 at 273 K and 1.0 bar, outperformed the corresponding single MOF and COF. Additionally, the highest I2 vapor uptake of the hybrid materials was determined to be 3.73 g·g−1 and it increased with the increase of the coating amount of Br-COFs. This work presents the successful regulation of the adsorption performance by the rational fabrication of novel hybrid MOFs@COFs interface.

engineering, chemical, environmental