Selective Photodegradation on Dual Dye System by Recoverable Nano SnO2 Photocatalyst

D. Venkatesh,S. Pavalamalar,K. Anbalagan

DOI: https://doi.org/10.1007/s10904-018-01069-w

IF: 3.518

2019-01-21

Journal of Inorganic and Organometallic Polymers and Materials

Abstract:A facile co-precipitation technique was developed to prepare SnO2 nanoparticles using stannous chloride dihydrate (SnCl2⋅2H2O) and characterized. The photocatalytic efficiency of nano SnO2 was tested for degradation of Rhodamine B: C28H31ClN2O3 + (nano SnO2/λ = 254 nm) + reactive species (•O2−, •OH, •OOH) → H2O + CO2. In addition, mixture of Rhodamine B (RhB) and malachite green oxalate (MGO) were selected as the dual dye system (model pollutants) and their influencing factors such as concentration of mixtures (RhB + MGO), catalyst dosage, intensity of light source (254 and 365 nm), pH were also studied. Blank experiment (without catalyst) and surface adsorption indicates that Rhodamine B degrades at relatively very slow rate with k = 2.30 × 10−3 min−1 and k = 2.4 × 10−3 min−1 respectively. However, nano SnO2 induces a large increment in degradation rate corresponding with k = 4.0 × 10−3 min−1 (RhB = 8.69 × 10−6 M, catalyst 50 mg/100 mL, λ = 254 nm) and mixed dyes kRhB = 18.96 × 10−3 min−1 and kMGO = 26.5 × 10−3 min−1 were obtained. Further, the reusability of the catalyst was sustained up to three cycles and verified with XRD pattern.

polymer science