Effect of steel wool fibers on mechanical and induction heating response of conductive asphalt concrete

Mohammad M. Karimi,Masoud K. Darabi,H. Jahanbakhsh,Behnam Jahangiri,John F. Rushing

DOI: https://doi.org/10.1080/10298436.2019.1567918

2019-01-29

International Journal of Pavement Engineering

Abstract:This study characterises the mechanical, rheological, induced heating, and induced healing behaviour of asphalt concrete containing steel wool fibers (SWFs) as the conductive constituent. Induced heating of asphalt concrete through the electromagnetic field is a novel method to heal the damage induced in asphalt concrete. Previous studies used high contents of the SWF as the conductive material to improve the sensitivity of the asphalt concrete to the electromagnetic radiations. Experimental tests conducted in this study (e.g. uniaxial strength, indirect tension, semi-circular bending tests) show that the addition of 0.2 (wt)% SWF meets both the heating and healing requirements. The relatively low amount of SWF resulted in considerably less adverse effects on the mechanical and rheological properties of asphalt concrete comparing to higher percentages of SWF (e.g. 1.5 (wt)% of SWF). Tests conducted on different specimen sizes of asphalt concrete reveal substantial effects of specimen dimension (volume) on the heating rate that should be considered in the evaluation of asphalt concrete induction heating under electromagnetic power. In addition, it is shown that using 0.2 (wt)% SWF significantly reduces the effect of corrosion on induced heating of conductive asphalt concrete materials. Experimental results demonstrate that the tensile strength ratio (TSR) decreases from 25% for 1.5% SWF to 7% for 0.2% SWF.

construction & building technology,engineering, civil,materials science, characterization & testing