Dephosphorization kinetics of high-P-containing reduced iron produced from oolitic hematite ore

Liwei Liu,Guofeng Li,Yanfeng Li,Libing Zhao

DOI: https://doi.org/10.1515/htmp-2022-0017

2022-01-01

High Temperature Materials and Processes

Abstract:Abstract To comprehensively utilize Fe and P in oolitic hematite ore, an innovative method was proposed to enhance P enrichment in the reduced iron during the reduction process. The reduced iron was then converted to low-P-containing molten iron and high-P-containing slag in the presence of CaO–SiO 2 –FeO–Al 2 O 3 slag. In this study, the P content of the final iron after 0–1,800 s dephosphorization was investigated at different slag composition conditions, and the dephosphorization kinetics of the reduced iron was analyzed. The results showed that the P content of the final iron sample decreased rapidly within 600 s of dephosphorization and became almost constant with increasing dephosphorization time to 1,800 s. The basicity, FeO content, and Al 2 O 3 content also affected the dephosphorization rate of the reduced iron. The apparent dephosphorization rate constant ranged from 1.141 × 10 −3 to 2.363 × 10 −3 g·(cm 2 ·s) −1 , and the overall mass transfer coefficient ranged from 2.47 × 10 −3 to 3.38 × 10 −3 cm·s −1 . The rate-controlling step of the dephosphorization process was the mass transfer of P in both the slag and iron phases. The findings of this study provide a theoretical basis for the utilization of refractory oolitic hematite ore.

materials science, multidisciplinary