Esterification modification and characterization of polyvinyl alcohol anion exchange membrane for direct methanol fuel cell

Xingyuan Huang,Jilin Wang,Lulu Wang

DOI: https://doi.org/10.1007/s10965-022-02958-y

IF: 3.061

2022-02-26

Journal of Polymer Research

Abstract:A series of anion exchange membranes (AEMs) with high conductivity and stable chemical properties were prepared by using polyvinyl alcohol phytate (PPVA) as the polymer matrix, 1,4-diglycidyl butane ether (DGBE) as the crosslinking agent and 2,3-epoxypropyl trimethylammonium chloride (EPTMAC) as the quaternization reagent. The chemical structure of the AEMs synthesized in this paper was characterized by ATR-FTIR to determine the successful preparation of the membranes. Additionally, the mechanical property, OH− conductivity, alkaline stability, and single-cell performance of the membrane was also discussed. Based on our results, when the molar ratio of polyvinyl alcohol (PVA) to PA is 2:1, the content of DGBE is 10%, the maximum tensile strength (19.0 MPa) of the membrane was obtained, the anionic conductivity can reach up to 0.594 S·cm−1 and the power density reaches 122 mW·cm−2 at 80 °C. Moreover, the good alkali resistance stability of AEMs was also proved, which was due to the conductivity of the QPPVA2-DGBE10% membrane can remain at around 80.7% of the initial conductivity when it was immersed in a 6 mol·L−1 KOH solution for 168 h at 60 °C. Compared with the commercial Nafion®-115 membrane, the prepared composite membranes synthesized in this paper have a lower methanol permeability in 3 mol·L−1 methanol at 60 °C, which is only 8.1% ~ 13.7% of Nafion®-115 membrane.

polymer science