Application of experimental design in the synthesis of 1-butanol from ethanol on mixed oxide catalysts at different mg/al molar ratios
Jana M. SimõesHeveline EnzweilerElisa Barbosa-CoutinhoMarcio SchwaabNina P. G. Salaua Departamento de Engenharia Química,Centro de Tecnologia,Universidade Federal de Santa Maria. Avenida Roraima,1000,CEP 97105–900,Santa Maria,RS,Brasilb Departamento de Engenharia de Alimentos e Engenharia Química,Universidade do Estado de Santa Catarina,Rua Fernando de Noronha,km 573,89870- 000,Pinhalzinho,SC,Brasilc Departamento de Físico-Química,Instituto de Química,Universidade Federal do Rio Grande do Sul. Av. Bento Gonçalves,9500,91501-970,Porto Alegre,RS,Brasild Departamento de Engenharia Química,Escola de Engenharia,Universidade Federal do Rio Grande do Sul. Rua Ramiro Barcelos,2777,Prédio 22202,90035-007,Porto Alegre,RS,Brasil
DOI: https://doi.org/10.1080/00986445.2024.2349672
2024-05-11
Chemical Engineering Communications
Abstract:1-Butanol, primarily sourced from petroleum, is currently being considered as a viable alternative to gasoline. Various pathways for synthesizing 1-butanol from renewable raw materials have been explored, with a particular focus on the Guerbet reactions. This study aimed to investigate the synthesis of 1-butanol from ethanol using Mg/Al mixed oxides derived from layered double hydroxides with Mg/Al molar ratios of 3:1, 5:1, 8:1, and 10:1. The catalysts were analyzed through X-ray diffraction, X-ray fluorescence, N 2 adsorption, scanning electron microscope and energy-dispersive X-ray spectroscopy. Catalytic reaction tests were performed according to a Central Composite Rotatable Design (CCRD) with three replicates at the central point (CP). Among the catalysts tested at CP, the mixed oxides with Mg/Al molar ratios of 3:1 and 5:1 exhibited the most promising results, displaying similar ethanol conversion, and 1-butanol selectivity. This similarity underscores their well-balanced combination of both acidic and basic sites. However, further assessment through a deactivation test revealed that the mixed oxides with Mg/Al molar ratio of 5:1 held the most potential for long-term 1-butanol synthesis from ethanol, thanks to its superior stability and sustained activity. Using this catalyst, other reaction tests were carried out following the CCRD, varying N 2 feed flowrate, ethanol molar content in feed flowrate, and temperature. The results indicated that an increase in ethanol conversion directly correlated with higher temperatures, while the 1-butanol selectivity depended on both the N 2 feed flowrate, ethanol molar content in feed flowrate, highlighting the importance of a well-balanced combination of both acidic and basic sites.
engineering, chemical