Mechanical Properties and Impermeability Strength Evolution of the Consolidated Body of Fiber-Modified Coal-Based Solid Wastes Grouting Materials
Junmeng Li,Yanli Huang,Yahui Liu,Hao Wang,Yachao Guo,Qihang Li
DOI: https://doi.org/10.1016/j.conbuildmat.2024.138556
IF: 7.4
2024-01-01
Construction and Building Materials
Abstract:Coal mining has raised the issues of groundwater loss and coal-based solid waste discharge. To realize the protection of water resources and rational utilization of coal-based solid wastes, coal-based solid waste was utilized as the primary raw material, and fibers were incorporated to fabricate grouting materials for sealing mining-induced fractures in this study. Specifically, coal gangue (CG), fly ash (FA), ordinary Portland cement (OPC), and sulfoaluminate cement (SAC) were employed to prepare coal-based solid waste grouting (CSWG) materials, and glass fiber (GF), copper-coated steel fiber (CCSF), polyvinyl alcohol fiber (PVA), and basalt fiber (BF) were used as reinforcement materials to develop the fiber-modified coal-based solid waste grouting (FCSWG) materials. By optimizing the composite cement ratio (OPC: SAC), fiber types, and fiber content, the workability, mechanical strength, and impermeability evolution of F-CSWG materials were investigated. The results show that compared to CSWG materials with single cement, the ratio of composite cement significantly affects the workability of the CSWG slurry, mainly manifested as the reduction of flowability and the shortening of setting time. When the SAC content is 40 %, the slurry fluidity exhibits the lowest value of 26.8 cm, and the initial setting time and the final setting time drop to the valley value of 33 min and 69 min, respectively Besides, the mechanical strength and impermeability of the CSWG material are deteriorated to varying degrees after the addition of SAC. After adding different types of fibers, the flowability and setting time of the F-CSWG slurry gradually decrease with the increase of fiber content, while its mechanical strength and impermeability first increase and then decrease. All four kinds of fibers can improve the performance of grouting materials, with varying degrees of improvement. The addition of 0.4 % GF yields optimal properties for F-CSWG materials, resulting in a notable enhancement of 25.1 % and 57.1 % in compressive strength and impermeability.