Abstract:Abstract Most of the recent nanodevices are fabricated by using high-efficiency deposition methods and patterned via high-resolution lithography. However, there are drawbacks for the methods including small-scale product, high cost consumption, and multi-step processes. To reduce these disadvantages, this work focuses on the usage of sol-gel synthesis and spin coating method to fabricate ZnO seed layer onto glass substrates. All of substrates were patterned by conventional UV photolithography at exposure time of 7 seconds, then ZnO nanorods were hydrothermally grown at 90°C for 2, 3, and 4 hours, respectively. All of samples were characterised by scanning electron microscope (SEM) which revealed the sharp and smooth tip hexagonal structure at different hydrothermal time. The evolution of the nanorods’ growth was investigated, and the diameters were estimated. Moreover, crystal quality was revealed by x-ray diffractograms. It was clear that the domination of c-axis plane occurred for all the samples associates with the crystallinity of the nanostructures. This indicated escalating of the non-monodirectional growth plane in increasing nanorods’ diameter as the nanorods are polycrystal. Furthermore, the optical properties of the samples were observed by UV-visible spectroscopy and photoluminescence technique (PL). UV-visible spectroscopic data showed diminishing of the energy band gap when the diameter grew up. PL data revealed the reduction of the intensity ratio at near-band-edge peak versus oxygen vacancy peak. This information pointed to the decreasing trend of the crystal quality with escalating growth time.

Micro structure of hydrothermal ZnO rods on micro cantilever surface

Effects of Electrodeposition Electrolyte Concentration on Microstructure, Optical Properties and Wettability of ZnO Nanorods

Effect of Reaction Temperature on Surface Morphology and Photoelectric Properties of ZnO Grown by Hydrothermal Method in Mixed Solvent

Morphology Investigation of Hydrothermally Prepared ZnO Micro-Crystals Influenced by Cu2+ Ions

Effect of Electrodeposition Time on Microstructure, Wettability and Optical Properties of ZnO Nanorod Arrays

Conversion of large-scale oriented ZnO rod array into nanotube array under hydrothermal etching condition via one-step synthesis approach

Sequential Occurrence of ZnO Nanopaticles, Nanorods, and Nanotips During Hydrothermal Process in a Dilute Aqueous Solution

Influence of hydrothermal time on structural properties of ZnO nanorods grown on spin-coated ZnO seeding layer

Hydrothermal Synthesis of Well-Aligned ZnO Nanorod Arrays on Silicon

The kinetics of the hydrothermal growth of ZnO nanostructures

Microcosmic Growth Process of ZnO Microrods

Fabrication of ZnO nanorods on O-polar ZnO layers grown by molecular beam epitaxy and electrical characterization using conductive atomic force microscopy

Nano/Micro-Structured ZnO Rods Synthesized by Thermal Chemical Vapor Deposition with Perpendicular Configuration

Hexagonal Crown-Capped Zinc Oxide Micro Rods: Hydrothermal Growth and Formation Mechanism.

Growth and characterization of ZnO nanoflakes by hydrothermal method: effect of hexamine concentration

Controllable Growth of Zinc Oxide Single-Crystal Hexagonal Microtubes by Hydrothermal Synthesis

Formation of ZnO Rods with Varying Diameters from Ε-Zn(oh)2

Hydrothermal self-assembling of ZnO nanorods into sphere-like superstructures and their optical characteristics

Fabrication and Optical Character of High Quality ZnO Microrods

Forming Extremely Smooth Zno Thin Film on Silicon Substrates for Growth of Large and Well-Aligned Zno Rods with the Hydrothermal Method

Facile growth of high transmittance ZnO micro-rod clusters on indium tin oxide by a wet-chemical synthesis method