Abstract:A novel bio-based benzoxazine resin (phenolphthalein-furfuramine-benzoxazine , PTL-F-BOZ) , used bio-based furfurylamine , phenolphthalein , and paraformaldehyde as raw materials , was synthesized and characterized by Fourier transform infrared spectroscopy (FTIR) , nuclear magnetic resonance (H-1 NMR and C-13 NMR) . The curing , thermal and flame retardant properties were analyzed by differential scanning calorimetric (DSC) , thermogravimetric analyzer (TG) , limiting oxygen index (LOI) , vertical burning test, microscale combustion calorimetry (MCC) , cone calorimeter(Cone) and scanning electron microscope (SEM) . The DSC curve of PTL-F-BOZ showed a two-stage curing with two maxima at 224 and 251 degrees C respectively, and had lower curing temperature than that of the traditional fossil-based bisphenol benzoxazine bisphenol A-aniline benzoxazine (bisphenol A-aniline-benzoxazine , BPA-A-BOZ) . The presence of the furan ring in the furfurylamine increased the cross-linking density of polymer, retarded the rearrangement reaction from the phenoxy structure to the phenol structure, and resulted in two curing peaks in the DSC curve of PTL-F-BOZ. Under nitrogen and air atmospheres, the temperatures of 5% mass loss (T-5%) for PPTL-F-BOZ resin were 380 and 370 degrees C , respectively and the residual chars at 800 degrees C were 63. 0% and 10. 5% , respectively. Compared with PBPA-A-BOZ resin, PPTL-F-BOZ resin both possessed higher T-5% and residual char of 800 degrees C. From the DTG curve , the maximum mass loss rates of two decomposition stage (Peak 1 and Peak 2 values) of PPTL-FBOZ resin were 0. 67%/min and 3. 28%/min, which were only 7. 38% and 63. 44% of PBPA-A-BOZ (9. 07%/min and 5. 17%/min) under nitrogen atmosphere , and those were also the same under air atmosphere. LOI of PPTL-F-BOZ resin was 36. 2%, which was higher than that of PBPA-A-BOZ resin. Meanwhile, in the UL-94 test, PPTL-F-BOZ resin extinguished quickly and released less smoke during combustion process, and the original morphology was kept well and a stable carbon layer was formed after burning. Its first ignition time(t(1)) and second ignition time(t(2)) were 1. 4 and 8. 5 s , respectively , far smaller than the maximum permissible values of 10 s, and a UL94 V-0 rating was also achieved. Hence, PPTL-F-BOZ resin showed excellent thermal and flame retardant properties.

Synthesis and thermal properties of silicon-containing benzoxazine

Preparation and properties of silicon-containing benzoxazine with high thermal stability

Synthesis and Properties of a Novel Bio-based Benzoxazine

Novel Full Bio-Based Phloroglucinol Benzoxazine Resin: Synthesis, Curing Reaction and Thermal Stability

Synthesis and Properties of a Novel Bio‐based Benzoxazine Resin with Excellent Low‐temperature Curing Ability

Synthesis of Aromatic Diamine-Based Benzoxazines and Effect of Their Backbone Structure on Thermal and Flammability Properties of Polymers

Synthesis, characterization, and thermal properties of benzoxazine monomers containing allyl groups

Film-forming Characteristics and Thermal Stability of Low Viscosity Benzoxazines Derived from Melamine

Polymerization behaviors and properties of benzoxazine resins based-on meta-substituted anilines

Synthesis, Polymerization Kinetics and Thermal Properties of Benzoxazine Resin Containing ortho-Maleimide Functionality

A Novel Acetylene-Functional/Silicon-Containing Benzoxazine Resin: Preparation, Curing Kinetics and Thermal Properties

Synthesis, Properties of Novel Benzocyclobutene-Functionalized Siloxane Thermosets

Synthesis of a Bisbenzylideneacetone-Containing Benzoxazine and Its Photo- and Thermally Cured Thermoset

Synthesis, characterization, and polymerization of brominated benzoxazine monomers and thermal stability/flame retardance of the polymers generated

Synthesis, ring-opening polymerization, and properties of benzoxazines based on o- and p-hydroxybenzyl alcohols

Thermally Stable, Flame Retardant, Low‐dielectric Constants, and Flexible Thermosetting Resins Based on a Tetra‐functional Benzoxazine Compound Possessing a Cyclic Siloxane Core

Synthesis and characterization of novel bio-based benzoxazines from eugenol

Thermally activated polymerization behavior of bisphenol-S/methylamine- based benzoxazine

Thiophene-Rich Benzoxazines with an Amide Moiety: Integration of Structural and Hydrogen Bonding Influence on the Polymerization Mechanism by Experimental and Computational Studies

Synthesis of Daidzein and Thiophene Containing Benzoxazine Resin and Its Thermoset and Carbon Material

Synthesis and properties of a benzoxazine monomer containing maleimide and biphenyl groups