Abstract:Skutterudite compounds have excellent thermoelectric performance in the intermediate-to high temperature range. Their lattice thermal conductivity can be reduced by intensifying phonon scattering through independent vibrations of the guest atoms, by filling the voids within the lattice. Furthermore, the thermoelectric figure of merit (ZT) can be enhanced by optimizing the carrier concentration through charge compensation between transition elements. In this study, we compared the thermoelectric properties of p-type filled skutterudite materials, R y Fe 4-x Co x Sb 12 , where R represents rare-earth elements (La/Ce/Pr/Nd/Yb), which were filled in the voids, and Co was charge-compensated at the Fe site. In the case of La y Fe 4-x Co x Sb 12 , the introduction of La filling and Co doping led La 0.9 Fe 3 CoSb 12 to exhibit a high power factor and low thermal conductivity (ZT = 0.67 at 723 K). In the case of Ce y Fe 4-x Co x Sb 12 , in addition to Ce filling, the substitution of Co for Fe resulted in additional lattice scattering, leading to a decrease in thermal conductivity. However, CeFe 4 Sb 12 exhibited a maximum performance of ZT = 0.70 at 823 K. In the case of Pr y Fe 4-x Co x Sb 12 , the thermal conductivity was reduced through phonon scattering induced by Pr filling and additional lattice scattering caused by Co substitution; as a result, Pr 0.8 Fe 3 CoSb 12 exhibited ZT = 0.89 at 723 K. In the case of Nd y Fe 4-x Co x Sb 12 , the phonon scattering was enhanced by adjusting the filling of Nd and substitution of Co, resulting in a lower thermal conductivity; Nd 0.9 Fe 3.5 Co 0.5 Sb 12 exhibited ZT = 0.91 at 723 K. For Yb y Fe 4-x Co x Sb 12 , Yb 0.9 Fe 3 CoSb 12 exhibited a thermoelectric performance of ZT = 0.56 at 823 K. In addition, in this study, for the fabrication (application) of thermoelectric modules, the p-type Nd 0.9 Fe 3.5 Co 0.5 Sb 12 skutterudite, which exhibited the best thermoelectric performance, was prepared in bulky compacts to verify the uniformity and reproducibility of its thermoelectric performance.

Effects of sintering temperature on microstructure and thermoelectric properties of Ce-filled Fe4Sb12 skutterudites

Ce Filling Limit and Its Influence on Thermoelectric Performance of Fe3CoSb12-Based Skutterudite Grown by a Temperature Gradient Zone Melting Method

Thermoelectric Properties of P-Type Skutterudites (pr0.25nd0.75)(x)fe3cosb12 by Levitation Melting and Spark Plasma Sintering

Unique surface structure resulting in the excellent long-term thermal stability of Fe4Sb12-based filled skutterudites

Rapid fabrication of pure p-type filled skutterudites with enhanced thermoelectric properties via a reactive liquid-phase sintering

Impurity Removal Leading to High-Performance CoSb 3 -Based Skutterudites with Synergistic Carrier Concentration Optimization and Thermal Conductivity Reduction

Skutterudite: Reproducibility of Thermoelectric Performance of P-type R y Fe 4-x Co x Sb 12 Bulky Compacts

Thermoelectric Property of Fine-Grained CoSb3skutterudite Compound Fabricated by Mechanical Alloying and Spark Plasma Sintering

Synthesis and thermoelectric properties of double-filled skutterudites CeyYb0.5-yFe1.5Co2.5Sb12

Solubility design leading to high figure of merit in low-cost Ce-CoSb3 skutterudites

Thermoelelctric Properties of Nanostructured Skutterudite-Related Compounds

Effects of sintering temperature on thermoelectric properties of Cu1.8S bulk materials

Synthesis and High Temperature Thermoelectric Properties of Calcium and Cerium Double-Filled Skutterudites Ca0.1CexCo4Sb12

High-performance flexible p-type Ce-filled Fe3CoSb12 skutterudite thin film for medium-to-high-temperature applications

Synthesis Optimization and Thermoelectric Properties of S-Filled and Te-Se Double-Substituted Skutterudite under High Pressure

Enhanced High-Temperature Thermoelectric Performance in Te-Doped Electronegative Element-Filled Skutterudites via Suppressing Bipolar Effects and Enhanced Phonon Scattering

Solvothermal Synthesis and Thermoelectric Properties of Skutterudite Compound Fe 0.25 Ni 0.25 Co 0.5 Sb 3

Microstructure Evolution and Mechanical Properties of Melt Spun Skutterudite-based Thermoelectric Materials

The competition between phase stability and band gap in Yb-filled cobalt-free Fe4-Ni Sb12 skutterudites

Research progress of p-type Fe-based skutterudite thermoelectric materials

Magnetic Iron Doping in Cu2SnS3 Ceramics for Enhanced Thermoelectric Transport Properties