Abstract:Concerning the environmental hazards owing to the chemical-based synthesis of silver nanoparticles (AgNPs), this study aimed to investigate the possibility of synthesizing AgNPs on the surface polyacrylonitrile (PAN) nanofibers utilizing biomacromolecule lignin. SEM observations revealed that the average diameters of the produced nanofibers were slightly increased from ~512 nm to ~673 nm due to several factors like-swellings that happened during the salt treatment process, surface-bound lignin, and the presence of AgNPs. The presence of AgNPs was validated by transmission electron microscope (TEM) and X-ray photoelectron spectroscopy (XPS) analysis. The amount of synthesized AgNPs on PAN nanofibers was found to be dependent on both precursor silver salt and reductant lignin concentration. Fourier transform infrared-attenuated total reflectance (FTIR-ATR) spectra confirm the presence of lignin on PAN nanofibers. Although the X-ray diffraction pattern did not show any AgNPs band, the reduced intensity of the stabilized PAN characteristics bands at 2θ = 17.28° and 29.38° demonstrated some misalignment of PAN polymeric chains. The water contact angle (WCA) of hydrophobic PAN nanofibers was reduced from 112.6 ± 4.16° to 21.4 ± 5.03° for the maximum AgNPs coated specimen. The prepared membranes exhibited low thermal stability and good swelling capacity up to 20.1 ± 0.92 g/g and 18.05 ± 0.68 g/g in distilled water and 0.9 wt% NaCl solution, respectively. Coated lignin imparts antioxidant activity up to 78.37 ± 0.12% at 12 h of incubation. The resultant nanofibrous membranes showed a proportional increase in antibacterial efficacy with the rise in AgNPs loading against both Gram-positive S. aureus and Gram-negative E. coli bacterial strains by disc diffusion test (AATCC 147-1998). Halos for maximum AgNPs loading was calculated to 18.89 ± 0.15 mm for S. aureus and 21.38 ± 0.17 mm for E. coli. An initial burst release of silver elements within 24 h was observed in the inductively coupled plasma-atomic emission spectrometry (ICP-AES) test, and the release amounts were proportionally expansive with the increase in Ag contents. Our results demonstrated that such types of composite nanofibers have a strong potential to be used in biomedicine.

Preparation and characterization studies of modified cellulosic textile fabric composite with in situ-generated AgNPs coating

A Two-Step Preparation Method for Nanocrystalline Ag-decorated Cotton Fabrics and Their Antibacterial Assessment

Novel Synthesis of Ag NPs on Polymer Fabrics by a Green Method for Antibacterial Performance

Bio-functionalization of cotton, silk, and leather using different in-situ silver nanoparticle synthesis modules, and their antibacterial properties

Preparation and properties of cotton nanocomposite fabrics with in situ generated copper nanoparticles using Red sanders powder extract as a reducing agent

Green Synthesis of Silver Nanoparticles Transformed Synthetic Textile Dye into Less Toxic Intermediate Molecules Through LC-MS Analysis and Treated the Actual Wastewater.

Surface cationization of cellulose to enhance durable antibacterial finish in phytosynthesized silver nanoparticle treated cotton fabric

Colorless Antibacterial Cotton Fabrics Based on Silver Nanoparticles and Chitosan Complexes

Green synthesis of silver nanoparticles with black rice (Oryza sativa L.) extract endowing carboxymethyl chitosan modified cotton with high anti-microbial and durable properties

Optimized Incorporation of Silver Nanoparticles onto Cotton Fabric Using k-Carrageenan Coatings for Enhanced Antimicrobial Properties

In-situ synthesis and immobilization of silver nanoparticles on microfibrillated cellulose for long-term antibacterial applications

Preparation, characterization, and antibacterial activity of composite material: Cotton fabric/hydrogel/silver nanoparticles

Ultrasonically developed silver/iota-carrageenan/cotton bionanocomposite as an efficient material for biomedical applications

Towards multifunctional cellulosic fabric: UV photo-reduction and in-situ synthesis of silver nanoparticles into cellulose fabrics

Green approach for the fabrication of silver-oxidized cellulose nanocomposite with antibacterial properties

Fabricating Antibacterial and Antioxidant Electrospun Hydrophilic Polyacrylonitrile Nanofibers Loaded with AgNPs by Lignin-Induced In-Situ Method

Antibacterial and Antifungal Activity of Functionalized Cotton Fabric with Nanocomposite Based on Silver Nanoparticles and Carboxymethyl Chitosan

Preparation of Copper Nanoparticles Coated Cotton Fabrics with Durable Antibacterial Properties

Anchoring silver nanoparticles using catechol-derived resins: An efficient and versatile approach for producing durable antimicrobial fabrics

Endophytic Streptomyces laurentii Mediated Green Synthesis of Ag-NPs with Antibacterial and Anticancer Properties for Developing Functional Textile Fabric Properties

Synthesis and attachment of silver and copper nanoparticles on cellulose nanofibers and comparative antibacterial study