Influence of Zr and Cu content on the microstructure and coercivity in Sm(CobalFe0.1CuyZrx)8.5 magnets

W. Tang,Y. Zhang,G. C. Hadjipanayis,H. Kronmüller
DOI: https://doi.org/10.1063/1.373330
IF: 2.877
2000-05-01
Journal of Applied Physics
Abstract:The effect of Cu and Zr on the microstructure and coercivity of Sm(CobalFe0.1CuyZrx)8.5 magnets has been studied using magnetometry and transmission electron microscopy. For Zr-free samples, when y=0.088, a cellular microstructure is not formed. Instead a rod-like 1:5 phase is observed, distributed in the 2:17 matrix phase. For a sample with y=0.168, the cellular microstructure develops after a short aging. However, the cellular microstructure coarsens and becomes highly nonuniform and finally, breaks down with further aging. This leads to a reduction in coercivity from an optimal value of 5.6–2 kOe. After adding Zr(x=0.04), the cellular microstructure along with a lamellar phase can be formed even with a Cu content as low as 0.048 and the coercivity increases dramatically. Coercivities of up to 8.9 and 38.4 kOe are obtained for the y=0.048 and 0.168 samples, respectively. These results show that the formation of cellular structure strongly depends on the Cu content. But the formation of the lamellar phase can stabilize a uniform cellular microstructure over a wide range of cell size and help the redistribution of Cu at the cell boundaries, which is a key to obtain appropriate microstructures with high coercivity.
physics, applied
What problem does this paper attempt to address?