Morphological study of cellulosic hydrogel nanofiber for biomedical application

Eunjoo Ko,Ki Soo Park,Seokjoon Kim,Taeho Kim,Hyungsup Kim
DOI: https://doi.org/10.1007/s10570-019-02725-1
IF: 6.123
2019-09-06
Cellulose
Abstract:In this work, water-insoluble and biocompatible hydrogel nanoweb was prepared via electrospinning. Sodium carboxymethyl cellulose (CMCNa), the cellulose derivative with water solubility and biocompatibility, was electrospun with help of building polymer, poly(ethylene oxide) (PEO). After removal of PEO, the CMCNa in the nanoweb was ionically crosslinked by FeCl<sub>3</sub>. The viscosity of the mixed solution was decreased with the increase of PEO content mainly due to the smaller molecular size of PEO comparing to CMCNa. The reduced interaction resulted from small molecular size decreased the viscosity with the increase of PEO content. The PEO also improved the spinnability of the solution by screening repulsive force between the CMCNa molecules. As a result, the increase of PEO content resulted in the decreases of the viscosity and the fiber diameter simultaneously. After extraction of PEO, the diameter was significantly reduced. The surface of the nanowebs became bumpy after crosslinking and fiber diameter increased with the increase of crosslinking time. The chemical structure changes of the nanowebs during the process were analyzed by FT-IR spectra. The cytotoxicity of the nanoweb was also assessed using MTT assay. Furthermore, the drug release behaviors of the nanowebs were evaluated using UV–Vis spectrometer. The nanoweb with increased fiber diameter showed more sustained release behavior because of its low specific surface area.
materials science, textiles,polymer science, paper & wood
What problem does this paper attempt to address?