Abstract:Purpose: to determine the effect of temperature and duration of firing on the dissociation-reduction reaction of mineral components of manganese ores. Recovery of manganese ore is carried out in four stages, which are determined by temperatures: <150°C, 150°C - 300°C, 300°C - 480°C, above 480°C. Topicality. Ores and concentrates undergo a number of complex transformations during heat treatment (agglomeration, firing of pellets and briquettes, preheating). The nature of such transformations is largely determined by chemical, mineralogical and particle size distribution, as well as other properties of the source ore. In addition to external conditions (temperature, pressure, nature of recovery, gas flow rate), the reaction rate is influenced by the physicochemical properties of the renewable substance, its mineralogical composition, structure, surface condition. The kinetic features of the reduction of pure manganese oxides are difficult to apply to manganese ores and concentrates with a rather complex structure and chemical composition. Understanding the basic chemical processes occurring in the smelting of manganese alloys is important for finding and justifying technological solutions to increase the efficiency of smelting of alloys. Method. Kinetic studies at different temperatures and fractional composition of the components under study. Results. The available literature data clearly indicate the dependence of the kinetic parameters of the processes occurring when heating manganese oxides in reducing conditions, from their physicochemical nature. To a lesser extent, process performance differs for natural minerals, although the composition of minerals may vary depending on the place of extraction. In this paper, it seems more appropriate to study the transformations that occur with manganese ores when heated, to use as an object of study the natural minerals that are part of these ores. Experimental data obtained in the study of physicochemical characteristics of the reducing processes of natural minerals can be used in the analysis of ore reduction and improvement of ferroalloy production processes. Scientific novelty. Kinetic studies of the process of interaction of minerals with reducing gas were performed at a constant heating rate of 14 degrees in the temperature range of 25-1000°C. Oxide concentrate and natural minerals lose moisture in the first 5-6 minutes. Their recovery proceeded at high speeds at temperatures of 300-4000C. A significant increase in speed was observed during the transition from a temperature of 4000C to a temperature of 6000C. Subsequent heating at 2000C led to a small increase in the total process speed. The total weight loss of the samples during heat treatment consisted of weight loss due to dissociation of manganese dioxide, weight loss due to dehydration and dissociation of carbonates that are part of the concentrate, as well as oxygen loss due to reduction. Calculations showed that the temperature of the beginning of the dissociation of MnO2 in a helium atmosphere is 460K. Dissociation of pure MnO2 is thermodynamically possible in the studied temperature range. The final decomposition product can only be manganese oxide. Practical significance. The obtained experimental data allowed to draw a conclusion about the inefficiency of grinding of oxidative manganese materials smaller than to the fraction -2.0 +1.5 mm before their heat or reduction-heat treatment in the processes of preparation of the charge for melting manganese ferroalloys. Key words: manganese ore, minerals, dissociation, kinetics, ore fractions

Effect of Heating Rate on Decomposition Temperature of Goethite Ore

Thermal Decomposition of Hematite Ore Fines in Air

Advances in calcium carbonate thermal decomposition

Characterisation of Varying Iron Ores and Their Thermal Decomposition Kinetics Under HIsarna Ironmaking Conditions

Iron Ore Characterisation during High Temperature Thermal Processing

Insight of Reduction Roasting of a Low-Grade Goethitic Indian Iron Ore in a Rotary Kiln: Process Optimization and Characterization

The Temperature of Pretreatment on Microstructure Change of Lump Ore and Improvement of Metallurgical Properties

Use of Additives as Internal Heat Sources in Hematite Ore Pellets- A Review

Hematite Dissociation Mechanism and Kinetics in Iron Ore Pellets during Heat Treatment

Cracking and Microstructure Transition of Iron Ore Containing Goethite in Fe-C Melt Based on the HIsmelt Process

Conversion of mineral components manganese ore at temperature conditions of formation of agglomerates

Structural deterioration of iron ore particles during thermal processing

Thermal analysis of goethite

Thermal Decomposition Reaction Kinetics of Hematite Ore

Non-isothermal kinetic study of high-grade magnesite thermal decomposition and morphological evolution of MgO

Characterization of Graphite Oxide after Heat Treatment

The role of thermal improvements in indurating machines for pellet production from high-sulfur magnetite concentrate

An innovative study for pretreatment of high-phosphorus oolitic hematite via high-temperature heating: phase, microstructure, and phosphorus distribution analyses

The kinetics and reaction mechanism of the goethite to hematite transformation