Recovery of Rare Earth Element Cerium from Spent Automotive Exhaust Catalysts Using a Novel Method

Zhexuan Zhao,Zhaofu Qiu,Ji Yang,Benteng Ma,Zhen Li,Shuguang Lu,Yongye Xu,Limei Cao,Wei Zhang

DOI: https://doi.org/10.1007/s12649-019-00783-x

2019-09-16

Waste and Biomass Valorization

Abstract:This study developed a new method for the recovery of the rare earth element cerium (Ce) from spent automotive exhaust catalysts. The content of Ce was 5.31% (wt%) in the spent catalyst sample. Sulfuric acid (2 mol/L) and hydrofluoric acid (0.9 mol/L) were used as a mixed acid leaching agent to successfully decompose the ceria-zirconia solid solution of the catalyst, which is resistant to dissolve in acids. The leaching efficiency of Ce reached 99.25% under the optimal conditions of a catalyst particle size range of 76–96 µm, an S/L of 1/10 (w/v), a leaching temperature of 70 °C, a leaching time of 4 h, and 200 rpm. The Al³⁺ that was leached from the catalyst scrubbed F⁻ in the leachate, allowing the separate extraction of Ce⁴⁺ using di-2-ethylhexyl phosphoric acid (D2EHPA) in sulfuric acid media. Potassium permanganate (KMnO₄) with a concentration of 20% was added during the extraction to increase the oxidation rate of Ce and to diminish the reduction effect of the organic solution. The results indicated that 87.23% of Ce⁴⁺ was extracted into the D2EHPA-kerosene solution with a concentration of 0.8 mol/L D2EHPA, a stoichiometric quantity of KMnO₄ of 175%, and contact for 15 min at room temperature. Reduction stripping was performed using hydrochloric acid (2 mol/L) with 3% H₂O₂ to obtain the CeCl₃ solution. The recovered amount of Ce was 85.54% with high purity from the spent automotive exhaust catalyst.

environmental sciences