Abstract:In this paper, the workability, mechanical, ion leaching, and drying shrinkage properties of alkali-activated concrete with recycled coarse and fine aggregates were studied, and the pore structure and micro-morphology of different alkali-activated recycled aggregate concretes (AARACs) were characterized by using the mercury intrusion method and scanning electron microscopy, respectively. The experimental results showed that with the increase in the replacement rate of the recycled fine aggregate (RFA), the flowability showed a decreasing trend. Adding a certain amount of RFA improves the mechanical properties of the AARAC. The compressive strength at a curing age of 28 days was 65.3 MPa with 70 wt% RFA replacement. When the replacement rate of the RFA was 100 wt%, the maximum splitting tensile strength (4.5 MPa) was obtained at a curing age of 7 days. However, the addition of the RFA had little effect on the flexural strength of the AARAC. As an extension of the curing age, the splitting tensile strength, flexural strength, tension-to-compression ratio, and flexure-to-compression ratio all showed an increasing trend at first and then a decreasing trend. At a curing age of 7 days, the tension-to-compression ratio and flexure-to-compression ratio were both high (except for those of R100), indicating that the ductility and toughness of the specimen were improved. The addition of the RFA increased the drying shrinkage of the AARAC. At a curing age of 120 days, compared to the specimen without the RFA, the drying shrinkage rate of the specimen with the addition of 70 wt% RFA increased by 34.15%. As the curing age increased, the microstructure of the reaction products became denser, but the proportion of large-diameter pores increased. This study evaluated the application of RFA in AARAC. The experimental results showed that the RFA-based AARAC had acceptable mechanical and durability properties.

Time-dependent drying shrinkage model for concrete with coarse and fine recycled aggregate

Shrinkage and Creep of Sustainable Self-Compacting Concrete with Recycled Concrete Aggregates, Fly Ash, Slag, and Silica Fume

Drying shrinkage model for recycled aggregate concrete accounting for the influence of parent concrete

Behavior of FRP-Confined Recycled Brick Aggregate Concrete under Monotonic Compression

Fundamental behaviour of recycled aggregate concrete - Overview I: strength and deformation

A study on early shrinkage of recycled concrete

Properties of Recycled Aggregate Concrete with Different Water Control Methods

Experimental study and prediction model for autogenous shrinkage of recycled aggregate concrete with recycled coarse aggregate

RBSM-based Mesoscale Study of Frost Deterioration for Recycled Concrete Considering Air-Entrainment in Old and New Mortar

Experimental and Estimated Evaluation of Drying Shrinkage of Concrete Made with Fine Recycled Aggregates

Prediction of the Elastic Modulus and the Splitting Tensile Strength of Concrete Incorporating Both Fine and Coarse Recycled Aggregate

Five-phase Modelling for Effective Diffusion Coefficient of Chlorides in Recycled Concrete

Mechanical Properties and Early-Age Shrinkage of Ultra-High Performance Concrete Mortar with Recycled Fine Aggregate

Effect of Recycled Fine Aggregates on the Mechanical and Drying Shrinkage Properties of Alkali-Activated Recycled Concrete

The Impact of Fractal Gradation of Aggregate on the Mechanical and Durable Characteristics of Recycled Concrete

Influence of coarse coal gangue aggregates on elastic modulus and drying shrinkage behaviour of concrete

Testing and Prediction of the Strength Development of Recycled-Aggregate Concrete with Large Particle Natural Aggregate

Durability and shrinkage performance of self-compacting concrete containing recycled fine clay brick aggregate

Strength, shrinkage and creep and durability aspects of concrete including CO2 treated recycled fine aggregate

Experimental Study of Mechanical Properties and Theoretical Models for Recycled Fine and Coarse Aggregate Concrete with Steel Fibers

Coupled Effects of the Freeze-Thaw Cycles and Salt Erosion on the Performance of Recycled Aggregate Concrete