Beryllium-Free b-Rb2Al2B2O7 as a Possible Deep-Ultraviolet Nonlinear Optical Material Replacement for KBe2BO3F2
T. Tran,Nathan Z. Koocher,J. Rondinelli,P. Halasyamani
Abstract:A new beryllium-free deep-ultraviolet (DUV) nonlinear optical (NLO) material, b-Rb2Al2B2O7 (b-RABO), has been synthesized and characterized. The chiral nonpolar acentric material shows second-harmonic generation (SHG) activity at both 1064 and 532 nm with efficiencies of 2 KH2PO4 and 0.4 b-BaB2O4, respectively, and exhibits a short absorption edge below 200 nm. b-Rb2Al2B2O7 has a three-dimensional structure of corner-shared Al(BO3)3O polyhedra. The discovery of b-RABO shows that through careful synthesis and characterization, replacement of KBe2BO3F2 (KBBF) by a Be-free DUV NLO material is possible. Nonlinear optical (NLO) materials are of intense academic and technological interest attributable to their ability to generate coherent radiation over a range of different wavelengths. One topical subject of NLO crystal engineering is to directly access the deep-ultraviolet (DUV; l< 200 nm) through cascading second-harmonic generation. Coherent DUV radiation has applications in complex optical technologies, including photolithography, high-resolution spectroscopy, and laser cooling. The requirements for a viable DUV NLO material have been described earlier. To date, only KBe2BO3F2 is found to be amenable to direct generation of coherent light below 200 nm. There remains, however, the serious issue of using carcinogenic BeO in its synthesis. Also KBBF crystals exhibit weak interlayer interactions and large crystals have yet to be grown. A few Be-free noncentrosymmetric (NCS) borates have been discovered with very short absorption edges: LiB3O5 (LBO, 155 nm) [4] and CsB3O5 (CBO, 167 nm). However, both materials suffer from relatively small birefringences, 0.045 (LBO) and 0.063 (CBO) at 1064 nm that limits their use. b-BaB2O4 (bBBO), another well-known NLO material, exhibits a birefringence of 0.1127, however its absorption edge is 185 nm that makes the material impracticable for 6th-harmonic generation, that is, 1064 nm/6 = 177.3 nm. Aluminum borates are attractive candidates for replacing Be-borates or Be-borate fluorides in DUV NLO materials for three specific reasons. First, aluminum is far more benign that beryllium; its reagents are more accessible and present a lower health risk. Second, in oxides the tetrahedral coordination environment of the Al cation is similar to Be. As such, Be substitution by Al would be structurally possible while still retaining a short absorption edge. Finally, aluminum oxide reagents are far less expensive than the corresponding beryllium precursors. With respect to NCS aluminum borates, K2Al2B2O7 (KABO) has been reported and extensively investigated. KABO is reported to have a UV absorption edge of 180 nm with a birefringence of 0.070–0.074 at 589–405 nm. Centimeter size crystals have also been reported with a d11 = 0.45 pmV 1 through Maker fringe measurements. Also, partial substitution of Rb or Na for K resulted in K2(1 x)Rb2xAl2B2O7 (0.0< x< 0.75) (KRABO) or K2(1 x)Na2xAl2B2O7 (0.0< x< 0.6) (KNABO), respectively, that are isostructural to KABO. The SHG responses of KRABO and KNABO are comparable to KABO. Rb2Al2B2O7 (hereafter a-RABO) and Cs2Al2B2O7 (CABO) have also been reported. These isostructural materials are, however, centrosymmetric (CS). The centricity of the A2Al2B2O7 (A = K, Rb, Cs) materials is thought to be correlated with the size of the alkali cation. Centrosymmetry is observed as the size of the alkali cation increases. As a-RABO is CS, it was suggested that NCS bRABO would not exist. We report on the synthesis of NCS b-RABO (Rb2Al2B2O7). The material exhibits a powder SHG response at 1064 nm and 532 nm incident radiation with a shortwavelength absorption edge below 200 nm. Electronic structure calculations show that b-RABO exhibits sufficient birefringence and a moderate SHG coefficient to possibly replace KBBF. Inversion symmetry is lifted by the counter rotation of the Rb cations and AlO4 tetrahedra, which cooperatively stabilize distorted BO3 triangles. Our results indicate b-RABO could be an excellent candidate for Be-free optical technologies operating in the DUV using nonlinear light–matter interactions. b-RABO crystallizes in chiral nonpolar NCS space group (S.G.) P321 (Z = 3) and exhibits a 3D crystal structure consisting of corner-sharing Al(BO3)3O tetrahedra (Figure 1). The b-RABO crystal was twinned. By incorporating the twin law, the least-squares refinement significantly improved. The Al cations are connected to three oxygen atoms from three mono-dentated BO3 groups in the ab-plane, forming the [Al(BO3)]1 layers, and a bridging oxide along the c-direction. The strong interlayer bonding of b-RABO would resolve the layering tendency issue of KBBF and facilitate the crystal [*] Dr. T. T. Tran, Prof. P. S. Halasyamani Department of Chemistry, University of Houston 112 Fleming Building, Houston, TX 77204-5003 (USA)