Abstract:The ionic conductivity and electrochemical stability of the electrolyte layer as well as the capacity of cathode material play pivotal roles for enhancing the electrochemical performances of all-solid-state sodium batteries. Herein, Na11Sn2SbS11.5Se0.5 solid electrolyte with ionic conductivity of 6.6 × 10−4 S cm−1 is synthesized. Meanwhile, Na11Sn2SbS11.5Se0.5-Na3PS4 electrolyte bilayer is employed to address the unstability of Na11Sn2SbS11.5Se0.5 against sodium. Moreover, the optimized Co0.1Fe0.9S2 is used as cathode to further improve the capacity of the all-solid-state sodium batteries. Thus, the as-generated Co0.1Fe0.9S2/Na11Sn2SbS11.5Se0.5-Na3PS4/Na all-solid-state sodium battery exhibits high reversible capacity of 383.5 mAh g−1 after cycling at 20 mA g−1 for 30 cycles, enhanced rate capability with capacities of 454.6, 405.3, 256.6 and 115.7 mAh g−1 at 20, 50, 100 and 200 mA g−1 after the first activation cycle, respectively, and improved high rate cycling stability with capacity of 159.8 mAh g−1 after cycling at 100 mA g−1 for 100 cycles.

Cobalt-doped pyrite for Na11Sn2SbS11.5Se0.5 electrolyte based all-solid-state sodium battery with enhanced capacity