Abstract:Abstract The synthesis of ambient-cured sustainable geopolymer mortars (GMs) was studied throughout this work. To reduce carbon dioxide emissions, new materials must be used in the production of sustainable concrete and mortars. Many types of binders are used in the synthesis of GM and concrete (GPC), especially clay minerals. These clay minerals are considered sources of alumina and silica in GM and concrete. The geopolymerization process relies on the alkaline solution activating the alumino-silicate to produce geopolymer gel products. The palygorskite (PA) clay mineral, sodium hydroxide (NaOH), and sodium silicates (Na 2 SiO 3 ) were chosen as a binder (solid material) and alkaline activator solution to synthesize GM at ambient temperature. PA was thermally treated at 550, 650, 700, and 750°C, respectively, to convert into high-reactive PA (HRP) HRP550, HRP650, HRP700, and HRP750, respectively. The characteristics of PA clay, HRP powders, and HRP-based GM were evaluated using compressive strength (CS) testing, X-ray fluorescence analysis, c arbon footprint analysis, X-ray diffraction (XRD) diffractograms, Fourier transform infrared spectroscopy (FTIR) spectroscopy, scanning electron microscopy (SEM) images, and energy-dispersive X-ray spectroscopy (EDS) analysis. The maximum CS of 25.1 MPa was acquired for geopolymer synthesis utilizing HRP700-based GM cured at 30°C for 28 days. FTIR spectroscopy demonstrated that HRP-based GM showed the presence of Si–O, Al–O, and O–C–O bonds stretching vibrations in the alumino-silicate network. The results showed that the CO 2 emissions had a reduction in the HRP-based GM compared with the reference mix of ordinary Portland cement mortar (OPM). The percentage of reductions was 14.1, 13.7, 13.1, and 12.4 for HRP550, HRP650, HRP700, and HRP750, respectively, compared with the OPM mixture. SEM images/EDS analysis and XRD diffractograms confirmed the presence of sodium alumino-silicate hydrates, magnesium silicate hydrate, and calcium silicate hydrate gels with high quantities particularly in the HRP700-based GM than that in HRP550, HRP650, and HRP750, respectively. The results indicate the suitability of HRP calcined at 700°C (HRP700) in the synthesis of the GM.

Rice Husk Ash Derived Sodium Silicate Using Hydrothermal and Convection Heating Methods

Simultaneous effects of rice husk silica and silicon carbide whiskers on the mechanical properties and morphology of sodium geopolymer

Hydrothermal synthesis of sodium silicate from rice husk ash: Effect of synthesis on silicate structure and transport properties of alkali-activated concrete

Characterisation of cementitious composite materials based on calcined clay activated by silicate from rice husk ash and Ingessil silicate - activator: sodium hydroxide (NaOH)

Workability and durability analysis of waste based geopolymer concrete

Utilisation of Biosilica as Active Silica Source for Metakaolin-Based Geopolymers

Physical and mechanical properties of meta-halloysite-based geopolymer mortars

Synthesis and Characterization of Red Mud and Rice Husk Ash-Based Geopolymer Composites

Physico-Mechanical Evaluation of Geopolymer Concrete Activated by Sodium Hydroxide and Silica Fume-Synthesised Sodium Silicate Solution

Novel Foaming-Agent Free Insulating Geopolymer Based on Industrial Fly Ash and Rice Husk

Optimization and characterization of sustainable geopolymer mortars based on palygorskite clay, water glass, and sodium hydroxide

Experiment study on the mechanical properties and alkali silica reaction (ASR) of mortar blended rice husk ash (RHA)

Formulation of geopolymer binder based on volcanic-scoria and clay brick wastes using rice husk ash-NaOH activator: Fresh and hardened properties

Mechanical Properties of Geopolymers Synthesized from Fly Ash and Red Mud under Ambient Conditions

Geopolymerization of Red Mud and Rice Husk Ash and Potentials of the Resulting Geopolymeric Products for Civil Infrastructure Applications

Analyzing Influence of Mix Design Constituents on Compressive Strength, Setting Times, and Workability of Geopolymer Mortar and Paste

Strength and Microstructure Characteristics of Blended Fly Ash and Ground Granulated Blast Furnace Slag Geopolymer Mortars with Na and K Silicate Solution

High Performance Concretes with Highly Reactive Rice Husk Ash and Silica Fume

Effect of silica fume on rheology of slag-fly ash-silica fume-based geopolymer pastes with different activators

Thermal stability and microstructure of metakaolin-based geopolymer blended with rice husk ash

The Effect of Dry Mix Sodium Hydroxide onto Workability and Compressive Strength of Geopolymer Paste