Abstract:In order to improve the calorific value and reducibility of the syngas produced by traditional coal gasification technology, and to solve the problem of high cost of heat source in coal gasification, this paper proposes to use high-temperature copper slag as the heat carriers and catalyst for coal gasification, and CaO as the CO 2 adsorbent during the coal gasification reaction. In this way, the proportion of H 2 in the syngas gas can be increased, and the coal gasification reaction can be improved. In the experiment, the samples with different ratios were fully mixed, and then thermogravimetric experiment and gasification experiment were carried out. Through research, the following rules were found. The use of high-temperature copper slag as the heat source and catalyst in coal gasification can lead to a 20% increase in the final weight loss rate. Additionally, when CaO is used as the CO 2 adsorbent during the coal gasification reaction, a noticeable secondary weight loss occurs at around 600°C and can reach a maximum speed of 0.19%/min. The use of the C/S/CaO = 1/1/2 ratio can result in a maximum weight loss rate of 23%. Meanwhile, the C/S/CaO = 1/2/1 group has been shown to achieve a maximum weight loss speed of 0.5%/min, and the C/S/CaO = 1/1/1 group exhibits a maximum secondary weight loss speed of 0.32%/min. The samples after gasification experiment were analyzed by SEM, CaO produced clustered iron-based and porous structure on the surface of copper slag in gasification reaction. Based on the Coats-Redfern method, kinetics of gasification reaction is obtained, and the optimum fitting function is C2, mechanism functions didn't change with the variation of C/S/CaO. The research results suggest that CaO and copper slag can both enhance the coal gasification reaction. In addition, CaO is proven to be a more affordable and accessible CO2 adsorbent compared to other alternatives.

Effects of CaO on Two-Step Reduction Characteristics of Copper Slag Using Biochar as Reducer: Thermodynamic and Kinetics

Direct reduction of copper slag-carbon composite pellets by coal and biochar

The effect of CaO on coal gasification reaction with high-temperature copper slag as catalyst

Coupling kinetics of high-temperature carbothermal reduction of copper slag under carbon dioxide atmosphere

Effects of CaO, Al2O3 and MgO on Kinetics of Lead-Rich Slag Reduction

Carbothermic Smelting Reduction of Copper Slag for Fe and Cu Recovery Using Calcium Aluminate Refining Slag as the Modifier

Investigation of Reducing Magnetite in Copper Slag Using CO–CO2

Effect of Na2CO3 Addition on Carbothermic Reduction of Copper Smelting Slag to Prepare Crude Fe-Cu Alloy

Reduction of Copper Smelting Slag by Carbon for Smelting Cu-Fe Alloy

Research on kinetic of carbon reducing process of molten CaO-FeOx-SiO2 system

Copper Slag Assisted Coke Reduction of Phosphogypsum for Sulphur Dioxide Preparation

Investigation of Direct Reduction of Copper Slag Using Castor Oil as a Green Reductant: Metal Recovery, Reduction Characterization and Kinetic Analysis

Recovery of Iron from Copper Slag Using Coal-Based Direct Reduction: Reduction Characteristics and Kinetics

Thermodynamic and kinetic behaviours of copper slag carbothermal reduction process

A Novel Process to Upgrade the Copper Slag by Direct Reduction-Magnetic Separation with the Addition of Na2CO3 and CaO

Experimental Study on Preparation of Calcium Oxide by Coal Reduction of Calcium Sulfate in Carbon Dioxide Atmosphere

Pyrometallurgical Reduction of Copper Slag with Biochar for Metal Recovery

Co-modification of BOF Slag and Copper Slag to Recover Valuable Metals by Carbothermal Reduction

Research on Selective Reducing Impoverishment Process of Copper Slag

Recovery of Metals from Copper Smelting Slag Using Coke and Biochar

Kinetic and Thermodynamic Studies on Lead-Rich Slag Reduction at Various CaO/SiO2 Ratios