Abstract:Recycled aggregate concrete is beneficial to the development of urban green and sustainable development.Mechanical property is the basic property of concrete,and it is very important for the application of concrete in the actual engineering.In the northwest of China,the double effects of sulfate attack and freeze-thaw cycle will have adverse effects on the mechanical properties of concrete.Through respectively putting 0％,30％,50％,70％,100％ replacement rate of recycled aggregate concrete was put into 5％ sodium sulfate solution for circulation of 0,40,80,120,160,200,240,280 respectively.Then Inspect of concrete compressive strength,shear strength,splitting tensile strength,dynamic elastic modulus,quality.The result can be listed as follows:after 280 freeze-thaw cycles.The compressive strength loss ratio of recycled aggregate concrete with 100％ replacement ratio is the standard,0％,30％,50％,70％ replacement rate of recycled aggregate concrete compressive strength loss ratio decreased respectively by 36％,30％,21％,13％.The shear strength loss ratio of recycled aggregate concrete with 100％ replacement ratio is the standard,0％,30％,50％,70％ replacement rate of recycled aggregate concrete shear strength loss ratio decreased respectively by 25％,21％,15％,9％.The splitting tensile strength loss ratio of recycled aggregate concrete with 100％ replacement ratio is the standard,0％,30％,50％,70％ replacement rate of recycled aggregate concrete splitting tensile strength loss ratio decreased respectively by 18％,16％,9％,4％.The dynamic elastic modulus loss ratio of recycled aggregate concrete with 100％ replacement ratio is the standard,0％,30％,50％,70％ replacement rate of recycled aggregate concrete dynamic elastic modulus loss ratio decreased respectively by 23％,21％,14％,10％.The mass loss ratio of recycled aggregate concrete with 100％ replacement ratio is the standard,0％,30％,50％,70％ replacement rate of recycled aggregate concrete mass loss ratio decreased respectively by 7％,5％,3％,2％.Finally,combined with the experimental results,the mechanism of the effect of different substitution rates on the mechanical property in recycled aggregate concrete is analyzed in detail.It provides a reference for the application of recycled aggregate concrete in practical engineering.

Study on the Property and Mix Ratio of CA and L•SAC Recycled Aggregate Planted Concrete

Shrinkage and Creep of Sustainable Self-Compacting Concrete with Recycled Concrete Aggregates, Fly Ash, Slag, and Silica Fume

Study on the Effect of Fly Ash and Polycarboxylic Acid Water Reducer on the Properties of Recycled Concrete

Properties of Recycled Aggregate Concrete with Different Water Control Methods

Influence of Construction Conditions on Properties of Recycled Concrete

A study on early shrinkage of recycled concrete

Study on the Effect of Recycled Coarse Aggregate on the Shrinkage Performance of Green Recycled Concrete

Study on Mechanical and Shrinkage Properties of High Belite Sulphoaluminate Cement-Based Green Recycled Aggregate Concrete

Effect of Aggregate Size and Water/Cement on Compressive Strength and Physiological Performance of Planting Concrete

Study On Properities Of Recycled Concrete Aggregate And Influence Of It On Properities Of Concrete

Study on Durability of Recycled Large Aggregate Concrete

Effects of Mixture Proportions and Molding Method on the Performance of Pervious Recycled Aggregate Concrete

Study of mix design and performance of alkali-activated concrete with recycled concrete aggregate

Compressive Strength, Permeability, and Abrasion Resistance of Pervious Concrete Incorporating Recycled Aggregate

Effect of Recycled Fine Aggregates on the Mechanical and Drying Shrinkage Properties of Alkali-Activated Recycled Concrete

Effect of Mixed Recycled Aggregate on the Mechanical Strength and Microstructure of Concrete under Different Water Cement Ratios

Investigating the Effects of Recycled Micropowder and Aggregate on the Properties of Cement Stabilization of Crushed Aggregate (CSCA)

Effects of Different Factors on the Performance of Recycled Aggregate Permeable Pavement Concrete

Study on Mechanical Property of Recycled Aggregate Concrete with Different Replacement Ratio under the Combined Action of Sulfate Attack and Freeze-thaw Cycle

Durability of Recycled Concrete after Reinforcing the Aggregates with Permeable Crystalline Materials

Experimental Research on Plastic Shrinkage Cracking Properties of Recycled Fine Aggregate Concrete