Bimetallic Co–Ni alloy nanoparticles loaded on nitrogen-doped wrinkled carbon nanospheres as high-performance bifunctional ORR/OER electrocatalyst in alkaline media
Qiuping Zhao,Lixia Bao,haibing Wang,Di Dou,Yuanyuan Cong,Chunlei Li
DOI: https://doi.org/10.1007/s11581-024-05478-5
IF: 2.961
2024-05-24
Ionics
Abstract:Preparation of an advanced bifunctional oxygen electrocatalyst is important for fuel cells, water splitting, etc. Herein, we report an oxygen reduction reaction (ORR)/oxygen evolution reaction (OER) electrocatalyst with CoNi alloy nanoparticles uniformly distributed on nitrogen-doped carbon (N–C) nanospheres through a simple melamine-assisted pyrolysis strategy, in which a soft template approach is employed to prepare wrinkled N–C nanospheres. The Co 3 Ni 1 -N–C electrocatalyst exhibits higher onset potential (E 0 = 0.960 V vs. RHE (Reversible hydrogen electrode)), half-wave potential (E 1/2 = 0.81 V vs. RHE), and limiting diffusion current (j L = 5.5 mA cm −2 ) for ORR. Meanwhile, Co 3 Ni 1 -N–C electrocatalyst has a lower overpotential of 0.360 V vs. RHE at 10 mA cm −2 for OER, and a lower value for Tafel slope of 100 mV dec −1 , a potential difference between OER and ORR (ΔE = E j=10 -E 1/2 ) with a ΔE value of 0.779 V vs. RHE, which is close to the benchmark ΔE value of the combination of commercial noble metal catalysts (Pt/C-RuO 2 , 0.744 V vs. RHE). In addition, Co 3 Ni 1 -N–C also shows remarkable stability, maintaining a relative current of 81.45% after 10 h at 0.8 V. The relative current of Co 3 Ni 1 -N–C is also found to be stable, superior to commercial Pt/C by 34.5%. These excellent properties are due to its unique wrinkled structure, large surface area, and high content of CoNi-Nx and pyridine nitrogen active centers.
chemistry, physical,physics, condensed matter,electrochemistry