Abstract:How to effectively enhance the catalytic performance and simultaneously reduce the usage of Pt-based catalysts is always the goal of catalyst design for electrochemical energy devices. Platinum nanoclusters (Pt NCs) have aroused massive concerns in recent years because of the excellent activity of Pt-based materials themselves and the unique physical and chemical properties of nanoclusters. However, the studies on the synthesis, properties and applications of Pt NCs have been rarely reported. Here, we report a simple avenue to synthesize Pt nanoclusters through using K2PtCl4 as precursor and mercaptosuccinic acid (MSA) as not only ligand but also the reducing agent at the room temperature. Based on the matrix-assisted laser desorption ionization time of flight mass spectrometry (MALDI-TOF MS), the obtained Pt NCs have the composition of Pt21(C4O4SH5)21. By loading the Pt NCs on reduced graphene oxide nanosheets (rGO) and the following removal of MSA ligands upon annealing treatment, the obtained surface-clean Pt NCs/rGO exhibits excellent hydrogen evolution reaction (HER) catalytic performance and superior stability with Pt loading as low as 0.8 wt%. Especially, the HER mass catalytic activity of the Pt NCs/rGO is much higher than that of the 20.0 wt% commercial Pt/C catalyst. Meanwhile, this kind of cluster catalyst also shows large exchange current density (574 µA•cm−2) and high turn-over frequency (1.19 s−1). The experimental result in this work clearly indicates that Pt catalyst on cluster scale can obviously improve the catalytic performance. Therefore, this study provides an effective avenue to enhance the utilization of noble metals and to develop high-performance and cost-effective catalysts.

Confining Sub‐Nanometer Pt Clusters in Hollow Mesoporous Carbon Spheres for Boosting Hydrogen Evolution Activity

Platinum Single-Atom and Cluster Anchored on Functionalized MWCNTs with Ultrahigh Mass Efficiency for Electrocatalytic Hydrogen Evolution

Overwhelming the Performance of Single Atoms with Atomic Clusters for Platinum-Catalyzed Hydrogen Evolution

Synergistic Effect of Platinum Single Atoms and Nanoclusters Boosting Electrocatalytic Hydrogen Evolution

Platinum Cluster Decoration on Hollow Carbon Spheres for High-Efficiency Hydrogen Evolution Reaction

Pt21(C4O4SH5)21 clusters: atomically precise synthesis and enhanced electrocatalytic activity for hydrogen generation

Intermetallic Cu5Zr Clusters Anchored on Hierarchical Nanoporous Copper As Efficient Catalysts for Hydrogen Evolution Reaction

Stable Pt Atomic Clusters on Carbon Nanotubes Grafted with Carbon Quantum Dots As Electrocatalyst for H2 Evolution in Acidic Electrolyte

Pt Single-Atom collaborate with Pt Atom-Clusters by an In-Situ confined strategy for accelerating electrocatalytic hydrogen evolution

Pt Nanoparticle Embedded Metal-Organic Framework Nanosheets for Efficient Alkaline Hydrogen Evolution

Heterojunction‐Based Electron Donators to Stabilize and Activate Ultrafine Pt Nanoparticles for Efficient Hydrogen Atom Dissociation and Gas Evolution

Subnano-Sized Pt-Au Alloyed Clusters As Enhanced Cocatalyst for Photocatalytic Hydrogen Evolution.

Fcc/hcp PtNi Heterostructured Alloy Nanocrystals with Ultrathin Pt Shell for Enhanced Catalytic Performance Towards Hydrogen Evolution Reaction

Pt Nanoclusters Anchored on Ordered Macroporous Nitrogen-Doped Carbon for Accelerated Water Dissociation Toward Superior Alkaline Hydrogen Production

Synergistic Effect Between Co Single Atoms and Pt Nanoparticles for Efficient Alkaline Hydrogen Evolution

Significantly Enhanced Hydrogen Evolution Activity of Freestanding Pd‐Ru Distorted Icosahedral Clusters with Less Than 600 Atoms

A universal synthesis strategy for single atom dispersed cobalt/metal clusters heterostructure boosting hydrogen evolution catalysis at all pH values

Hollow carbon shells enhanced by confined ruthenium as cost-efficient and superior catalysts for the alkaline hydrogen evolution reaction

Highly Dispersed Quasi-1 Nm Ruthenium Nanoclusters on Hierarchical Nitrogen-Doped Carbon Nanocages Constructed by Surface-Constrained Sintering for Alkaline Hydrogen Evolution

In Situ Confinement Of Ultrasmall Pd Clusters Within Nanosized Silicalite-1 Zeolite For Highly Efficient Catalysis Of Hydrogen Generation

Ni<sub>3</sub>[Fe(CN)<sub>6</sub>]<sub>2</sub> nanocubes boost the catalytic activity of Pt for electrochemical hydrogen evolution