Multifunctional finishes on photochromic microcapsule-printed cotton fabrics using titanium oxide nanoparticles
Gobikannan Tamilmani,Venkhatesan D.,Santhosh P.,Tamilselvan M.,Suryappa Jayappa Pawar,Amin Hirenbhai Navinbhai
DOI: https://doi.org/10.1108/prt-09-2023-0079
2024-01-12
Pigment & Resin Technology
Abstract:Purpose This paper aims to study the combination of photochromic microcapsules, which use the ultraviolet (UV) rays for colour changing phenomena, and titanium oxide (TiO 2 ) nanoparticles (NPs), which block the UV rays by their photocatalytic activity in the sunlight on the cotton fabric. Design/methodology/approach The TiO 2 NPs mixed with photochromic printing paste are used for coating on cotton fabric and further curing is performed in a one-step process. The photochromic pigment printed fabric impregnated in a liquid solution is processed in a two-step process with two variables such as 1% TiO 2 and 2% TiO 2 . The characterization of samples was done with a UV transmittance analyser, surface contact angle, antimicrobial test and fabric physical properties. Findings The UV protection of TiO 2 -treated photochromic printed fabric was high and gives the ultraviolet protection factor rating of 2,000 which denotes almost maximum blocking of UV rays. The antibacterial activity of the one-step samples shows the highest 36 mm zone of inhibition (ZOI) against S. aureus (gram-positive) and 32 mm ZOI against E. coli (gram-negative) bacteria. The one-step sample shows the highest static water contact angle of 118.6° representing more hydrophobicity, whereas the untreated fabric is fully wetted (0.4°). In two-step processes, as the concentration of TiO 2 increased, the antibacterial activity, UV blocking and hydrophobicity became better. Originality/value This work achieves the multifunctional finishes by using photochromic microcapsules and NPs in a single process as a first attempt. The results inferred that one-step sample has achieved higher values in most of the tests conducted when compared to all other sample.
engineering, chemical,materials science, coatings & films,chemistry, applied