High-performance microwave absorption properties of Ti3SiC2/Al2O3 coatings prepared by plasma spraying

Dong Zhao,Shaoqiu Xia,YongGuang Wang,Mingdi Wang

DOI: https://doi.org/10.1007/s00339-019-3236-y

2020-01-01

Applied Physics A

Abstract:The Ti₃SiC₂/Al₂O₃ coatings were prepared by plasma spraying process for the microwave absorption application. The coatings showed a dense structure with a few pores and unmelted region, and the Ti₃SiC₂ distributes uniformly in the coatings. The XRD was used to identify the phase composition of the coatings. The results indicated that the as-sprayed Ti₃SiC₂/Al₂O₃ coatings were composed of α-Al₂O₃ and γ-Al₂O₃, Ti₃SiC₂, TiC and Ti₅Si₃. The TiC and Ti₅Si₃ phases resulted from the Ti₃SiC₂ decomposition during the plasma spraying process. The complex permittivity of Ti₃SiC₂/Al₂O₃ coatings enhanced significantly with increasing the Ti₃SiC₂ content. When the Ti₃SiC₂ content was 20 wt. % and the coating thickness was 1.3 mm, the RL value of the coating can reach a minimum of − 24.4 dB at 11.1 GHz and RL value ≤ − 10 dB bandwidth in the frequency range of 10.1–12.4 GHz. Spherical instrumented scratch had been carried out on the Ti₃SiC₂/Al₂O₃ coatings to investigate the single-point abrasive wear behavior. Typical brittle fracture such as microcracks in the residual groove and grain dislodgement was observed in Ti₃SiC₂/Al₂O₃ coatings.