Effect of Cobalt-Content on Mechanical Properties of Non-Equiatomic Co–Cr–Ni Medium Entropy Alloys

Shuhei Yoshida,Takuto Ikeuchi,Yu Bai,Nobuhiro Tsuji

DOI: https://doi.org/10.2320/matertrans.mt-mk2019004

2020-04-01

MATERIALS TRANSACTIONS

Abstract:Non-equiatomic high entropy alloys (HEAs) and medium entropy alloys (MEAs) are expected to have the potential to exhibit good mechanical properties due to abundant composition designs compared to equiatomic alloys. It has been reported that an equiatomic CoCrNi MEA shows better strength-ductility balance than CoCrFeMnNi HEA, and there is a possibility that the mechanical properties can be further improved by changing chemical composition. Among the constituent elements, cobalt (Co) has the effect of decreasing stacking fault energy (SFE). In this study, we clarified the effect of Co-content on mechanical properties of non-equiatomic Co–Cr–Ni MEAs with different amounts of Co through investigating deformation behaviors and deformation microstructures. Cox(CrNi)(100−x) (x = 20 (Co20), 40 (Co40), 60 (Co60) at%) MEAs were processed to very high plastic strains by high-pressure torsion (HPT) and subsequently annealed under proper conditions to obtain FCC single-phase and uniform fine grain sizes. Mechanical properties of the specimens with fully recrystallized microstructures were characterized by tensile tests at room temperature. Their deformed microstructures at different tensile strain levels were observed by electron microscopy. The result of the tensile tests showed that the work-hardening rate was enhanced with increasing the Co-content although early fracture before reaching plastic instability condition occurred in Co60. Planar slip of dislocations and deformation twinning were observed in Co20 (SFE = 30 mJ/m2), while, in addition to them, deformation-induced martensitic transformation to HCP ε-martensite was observed in Co40 having lower SFE (SFE = 10 mJ/m2), leading to higher work-hardening rate. By increasing Co-content (decreasing SFE) further, phase fraction of ε-martensite greatly increased in Co60 (SFE = 0 mJ/m2) compared with Co40, and early fracture occurred due to stress concentration at intersects between martensite and grain boundaries. The present results suggested that the mechanical properties of the present materials could be effectively designed by controlling the SFE.

materials science, multidisciplinary,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to explore the influence of cobalt content on the mechanical properties of non - equiatomic ratio Co - Cr - Ni medium - entropy alloys. Specifically, by changing the proportion of cobalt in the alloy, the researchers explored the influence of different cobalt contents on the mechanical properties (such as yield strength, tensile strength, uniform elongation and total elongation) of these alloys, as well as the microstructure mechanisms behind these property changes. The paper experimentally analyzed the microstructure changes of alloys with different cobalt contents during the deformation process, including phenomena such as dislocation slip, twin formation and ε - martensite transformation, and discussed how these microstructure characteristics affect the mechanical behavior of the alloys.

The main contribution of the paper lies in revealing that the mechanical properties of this type of alloy can be effectively controlled and designed by adjusting the cobalt content, especially by adjusting the stacking fault energy (SFE) to influence the deformation mechanism, thereby achieving the optimization of material properties. This finding is of great significance for the development of new materials with specific mechanical property requirements.