Abstract:In this work, new materials based on the blends of polyvinyl alcohol (PVA), polyvinyl pyrrolidone (PVP), chitosan (CS), and polydopamine (PDA) have been prepared. Fourier Transform Infrared Spectra have been conducted to verify the presence of individual components in the composite materials. EDX elemental analysis showed a clear view of the element's presence in the composite materials, with the maximum values for carbon and oxygen. Atomic force microscopy (AFM) was used to observe the surface topography and measure the surface roughness. In the case of the individual polymers, CS presented the higher value of surface roughness (Rq = 3.92 nm and Ra = 3.02 nm), and surface roughness was found to be the lowest in the case of polyvinyl pyrrolidone (PVP), and it was with values (Rq = 2.34 nm and Ra = 0.95 nm). PVA films presented the surface roughness, which was with the value (Rq = 3.38 nm and Ra = 2.11 nm). In the case of composites, surface roughness was highest for the composite based on PVA, PVP, and CS, which presented the value (Rq = 11.91 nm and Ra = 8.71 nm). After the addition of polydopamine to the polymeric composite of PVA, PVP, and CS, a reduction in the surface roughness was observed (Rq = 7.49 nm and Ra = 5.15 nm). The surface roughness for composite materials was higher than that of the individual polymers. The addition of PDA to polymeric composite (PVA/PVP/CS) led to a decrease in Young's modulus. The elongation percentage of the polymeric films based on the PVA/PVP/CS/PDA blend was higher than that of the blend without PDA (9.80% vs. 5.68% for the polymeric composite PVA/PVP/CS). The surface of polymeric films was hydrophilic. The results from the MTT assay showed that all tested specimens are non-toxic, and it was manifested by a significant increase in the viability of L929 cells compared with control cells. However, additional studies are required to check the biocompatibility of tested samples.

Adsorption of Dyes Using Poly(vinyl alcohol) (PVA) and PVA-Based Polymer Composite Adsorbents: A Review

Influence of polyvinyl alcohol on the surface morphology, separation and anti-fouling performance of the composite polyamide nanofiltration membranes

Preparation of highly hydrophilic PVA/SBA-15 composite materials and their adsorption behavior toward cationic dye: effect of PVA content

Synthesis, characterization and analysis of conducting polymer composites toward dye adsorption

Synthesis and Dye Adsorption Dynamics of Chitosan–Polyvinylpolypyrrolidone (PVPP) Composite

Characterization of Polyvinyl Alcohol (PVA) as Antimicrobial Biocomposite Film: A Review

Development of multifunctional hydrogel composite based on poly(vinyl alcohol-g-acrylamide) for removal and photocatalytic degradation of organic dyes

Adsorptive behaviors and mechanisms for removing three organic pollutants from aqueous solutions by polyvinyl alcohol/porous carbon composite hydrogels

The removal of methylene blue and maxilon blue dyes using a polyvinyl alcohol/poly(acrylic acid-co-acrylamide) composite hydrogel from water

Recent Advances in Poly(vinyl alcohol)-Based Hydrogels

Evaluation, optimization study, and life cycle assessment of novel eco-friendly PVA-based nanocomposite hydrogel adsorbents for methylene blue and paracetamol removal

Porous PVA/Zn–Fe–Mn oxide nanocomposites: methylene blue dye adsorption studies

New Composite Materials Based on PVA, PVP, CS, and PDA

PVA/AMPS hydrogels: Promising adsorbents for wastewater treatment with high efficiency and reusability

Amine functionalised graphene embedded polyvinyl alcohol (PVA) and PVA-chitosan hydrogel composites

Properties and Applications of Polyvinyl Alcohol, Halloysite Nanotubes and Their Nanocomposites

Effects of Poly (vinyl Alcohol) (pva) Content on Preparation of Novel Thiol-Functionalized Mesoporous Pva/Sio2 Composite Nanofiber Membranes and Their Application for Adsorption of Heavy Metal Ions from Aqueous Solution

Comparative Study on the Adsorption Characteristics of Anionic, Cationic, and Non-Ionic Dyes by PVDF-PVA/GO Composite Membrane

Preparation and Characterization of Gamma Radiation Assisted Poly-Vinyl Alcohol/Acrylic Acid/Poly-4-Styrene Sulphonic Acid Based Hydrogel: Application for Textile Dye Removal

The influence of graphene oxide content on adsorption of PVA/SA composite gel spheres

Preparation and characterization of new foam adsorbents of poly(vinyl alcohol)/chitosan composites and their removal for dye and heavy metal from aqueous solution