The role of CNC surface modification on the structural, thermal and electrical properties of poly(vinylidene fluoride) nanocomposites

Mikel Rincón-Iglesias,Erlantz Lizundia,Daniela M. Correia,Carlos M. Costa,Senentxu Lanceros-Méndez
DOI: https://doi.org/10.1007/s10570-020-03067-z
IF: 6.123
2020-02-26
Cellulose
Abstract:This work shows the effect of cellulose nanocrystal surface charge on the morphology, structure, thermal and dielectric properties of poly(vinylidene fluoride) nanocomposites. CNCs extracted through sulfuric acid hydrolysis were modified using sodium hydroxide and cationization treatments to yield CNCs with zeta-potential values of − 26.1 ± 3.7 and − 4.4 ± 0.3 mV in comparison with the original highly-negative − 45.2 ± 1.1 mV. Nanocomposites where then obtained through doctor-blade casting followed by room temperature drying. CNC incorporation allows obtaining PVDF with 100% of γ-phase. An increase of the real dielectric constant ε′, dielectric loss tan δ and AC conductivity was observed by increasing CNC content. More importantly, these values are further boosted upon CNC surface-modification, suggesting the pivotal role of the CNC–PVDF interface. We conclude that the sulfate half-ester removal increase the amount of exposed –OH groups with increase the amount of accumulated charges at the PVDF–CNC interfaces.Graphic abstractThe effect of cellulose nanocrystal (CNC) surface charge on the morphology, structure, thermal and dielectric properties of poly(vinylidene fluoride) (PVDF) nanocomposites is here shown. By removing the sulfate half-ester it is possible to increase the amount of exposed –OH groups, enhancing the accumulated charges at the PVDF–CNC interfaces and improving the electric performance.
materials science, textiles,polymer science, paper & wood
What problem does this paper attempt to address?