Abstract:Microstructure progression, in addition to excellent plasticity possessions of AZ31B-alloy procedure using four paths in asymmetric through various reductions, was studied to facilitate develops the deprived plasticity of alloy. The procedure was used for alloy of about 78μm grain size, with a prim thickness of 5mm. It was formed by using different ratios,1:1,1:1.4,1:1.8and1:2.2.The thinning were 20%,25%,30%, 35% to reduce thickness to 4.00mm, 3.750 3.500 And 3.2500 repetitively. The rolling method was completed by using equal rollers diameter at a constant temperature of 473 K and devoid of lubricating after heating the rollers to 373K; the method was finished through four routes. Path (U.D.), pattern "way was kept" stable and unmoved connecting continual passes; whereas pattern was turned 180o to direction connecting continual passes during path (R.D.); pattern (N.D.) was turned throughout 180° concerning the standard direction to the continual passes; pattern (H.Y.) was turned 180o to the rolling direction primary in addition to, subsequently turned 90° concerning the standard direction connecting continual undulating passes. A traditional rolling process was done under identical situations to evaluate the outcome; microhardness test was also completed. Visual microscopy was used to study of rolling parameters on the microstructure of the rolled pieces. The outcome of inspection explained to the alteration of the microstructure had been pretentious employing path, ratio and decrease area. At low proportion, large numbers of mirror image creation become visible, as reduction raises dynamical recrystallization happening on the identical twin and shear bands were encouraged. In contrast raised proportion caused a raise within the quantity of recrystallized grains furthermore improved the microstructure. Very fine grains construction had been improved while the alloy was rolled using H.Y. path at a proportion of (1: 1.8) and 25% decrease. Excellent plasticity possessions of patterns devoid of annealing were experienced in stress at 673.00 K along with next to room temperature at primary strain selection from 1 × 10 −3 s −1 to 2.2 × 10 −3 s −1 .

Microstructure evolution of AZ91 alloy processed by a combination method of equal channel angular pressing and rolling

Effect of Single-Pass Rolling on Microstructure and Mechanical Properties of AZ31 Alloy Processed by Equal Channel Angular Pressing

Obtaining Heterogeneous Microstructure and Enhanced Mechanical Properties in ECAP-Processed AZ61 Alloys via Single-Pass Rolling with Increased Rolling Reduction

Achieving single-pass high-reduction rolling and enhanced mechanical properties of AZ91 alloy by RD-ECAP pre-processing

Recrystallization Behavior and Mechanical Properties of Az31b Alloy During the Hot-Rolling Process

Equal-Channel Angular Pressing of Magnesium Alloy Az91 and Its Effects on Microstructure and Mechanical Properties

Microstructure and mechanical properties of AZ61 alloys with large cross-sectional size fabricated by multi-pass ECAP

Achieving ultra-fine grains and high corrosion resistance of Al-Zn-Mg-Cu alloy by ECAP and post cold rolling

Evolution of the Microstructure and Mechanical Properties of AZ31 Magnesium Alloy Sheets during Multi-Pass Lowered-Temperature Rolling

Effect of Asymmetric Cross Rolling on Microstructure and Mechanical Properties of AZ31 Magnesium Alloy

Enhanced mechanical properties of AZ91 magnesium alloy by asynchronously large-strain high-efficiency rolling with bimodal grain structure

Microstructural evolution and mechanical properties of AZ31 Mg alloy fabricated by a novel bifurcation-equal channel angular pressing

Effect of Symmetric and Asymmetric Rolling Processes on The Microstructure and Mechanical Properties of AZ31B Magnesium Alloy

Microstructure Evolution and Mechanical Properties of AZ31 Alloy with Accumulative Roll Bonding

Mechanical Properties and Texture Evolution During Rolling Process of an AZ31 Mg Alloy

Reduction per pass effect on texture traits and mechanical anisotropy of Mg–Al–Zn–Mn–Ca alloy subjected to unidirectional and cross rolling

Microstructure and Tensile Properties of A Mg-Zn-Y-Zr Alloy Containing Quasicrystal Phase Processed by Equal Channel Angular Pressing

Impact of Equal Channel Angular Pressing on Mechanical Behavior and Corrosion Resistance of Hot-Rolled Ti-2Fe-0.1B Alloy

Microstructure and Mechanical Properties of Mg96Y3Zn1 Alloy Processed by Equal Channel Angular Pressing

Effect of Final Rolling Temperature on Microstructures and Mechanical Properties of AZ31 Alloy Sheets Prepared by Equal Channel Angular Rolling and Continuous Bending

Dry Sliding Wear of an AZ31 Magnesium Alloy Processed by Equal-Channel Angular Pressing