Hybrid Additive Manufacturing Technology: Induction Heating Cold Spray—Part II: Coating Mechanical Properties

R. Ortiz-Fernandez,B. Jodoin

DOI: https://doi.org/10.1007/s11666-020-01006-9

IF: 2.839

2020-03-03

Journal of Thermal Spray Technology

Abstract:Delamination of soft and ductile materials from hard substrates is a challenge when using the cold spray process. Additionally, the as-sprayed coatings often exhibit a significant reduction in ductility and a brittle behavior upon fracture. As a potential solution to these problems, a tunable hybrid additive manufacturing process was developed by coupling induction heating and the cold spray process. Pure aluminum was used as the soft feedstock powder, while Ti-6Al-4V was used as the hard substrate. In situ induction heating and substrate preheating temperature effects on the coating's properties were evaluated: micro-hardness, adhesion and tensile strength were assessed and compared to traditional cold spray coating's properties. A reduction of up to 20% was found in the coating's micro-hardness produced by the hybrid process. Additionally, the adhesion strength was drastically increased when using the hybrid process while tensile strength reached almost 3 times the total elongation of the specimens produced using the traditional cold spray process. These results open up the possibility of using this hybrid technique as an additive manufacturing process for bulk parts and coating production.

materials science, coatings & films