Very Robust Spray-Synthesized CsPbI 3 Quantum Emitters with Ultrahigh Room-Temperature Cavity-Free Brightness and Self-Healing Ability
Bo-Wei Hsu,Yung-Tang Chuang,Chun-Yuan Cheng,Chien-Yu Chen,Yen-Ju Chen,Alexandra Brumberg,Lin Yang,Yu-Sheng Huang,Richard D. Schaller,Lih-J. Chen,Chih-Sung Chuu,Hao-Wu Lin
DOI: https://doi.org/10.1021/acsnano.1c00733
IF: 17.1
2021-03-17
ACS Nano
Abstract:Although colloidal lead halide perovskite quantum dots (PQDs) exhibit desirable emitter characteristics with high quantum yields and narrow bandwidths, instability has limited their applications in devices. In this paper, we describe spray-synthesized CsPbI<sub>3</sub> PQD quantum emitters displaying strong photon antibunching and high brightness at room temperature and stable performance under continuous excitation with a high-intensity laser for more than 24 h. Our PQDs provided high single-photon emission rates, exceeding 9 × 10<sup>6</sup> count/s, after excluding multiexciton emissions and strong photon antibunching, as confirmed by low values of the second-order correlation function <i>g</i><sup>(2)</sup>(0) (reaching 0.021 and 0.061 for the best and average PQD performance, respectively). With such high brightness and stability, we applied our PQDs as quantum random number generators, which demonstrably passed all of the National Institute of Standards and Technology's randomness tests. Intriguingly, all of the PQDs exhibited self-healing behavior and restored their PL intensities to greater than half of their initial values after excitation at extremely high intensity. Half of the PQDs even recovered almost all of their initial PL intensity. The robust properties of these spray-synthesized PQDs resulted from high crystallinity and good ligand encapsulation. Our results suggest that spray-synthesized PQDs have great potential for use in future quantum technologies (<i>e.g</i>., quantum communication, quantum cryptography, and quantum computing).The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsnano.1c00733?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsnano.1c00733</a>.TEM images, size distribution histograms, and PL spectra of the <i>T</i>-PQDs and <i>C</i>-PQDs; PL spectra and PL QYs of a <i>S</i>-PQD solution before and after storage for 3 months; PL lifetime and saturation curve of a single II–VI semiconductor QD; NMR spectra of the <i>S</i>-PQDs and <i>T</i>-PQDs; PL time traces of multiple <i>S</i>-PQDs, <i>T</i>-PQDs, and <i>C</i>-PQDs; NIST randomness test results for the raw and unbiased data of the <i>S</i>-PQD QRNG; transient absorption measurements of <i>S</i>-PQD, <i>T</i>-PQD, and <i>C</i>-PQD films; fitted data of <a class="internalNav" href="#fig2">Figure </a><a class="internalNav" href="#fig2">2</a>f–h (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.1c00733/suppl_file/nn1c00733_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology