Study on the physico-mechanical properties of treated baobab fiber (Adansonia Digitata) nano-filler/epoxy composite

Maryann Ifeoma Uzochukwu,Wilson Uzochukwu Eze,Philip Garba,Michael Ifeanyichukwu Ugbaja,Henry Opara

DOI: https://doi.org/10.1007/s41939-020-00068-0

2020-03-13

Abstract:In this research, the physico-mechanical properties of epoxy/baobab nano-composite were studied. The fiber was treated with sodium hydroxide and the effect of fiber loading; 0 wt%, 10 wt%, 20 wt%, 30 wt%, 40 wt% and 50 wt% has been reported. 95.58% of the baobab fiber had particle distribution of falling between 10 and 100 nm. The fabrication of the composite was by casting on a glass mould and cold curing for 24 h at 25 °C. The result showed optimum mechanical properties with 10 wt% filler loading. Hardness and water absorption increased as the filler loading increases from 10 to 50 wt%. Abrasion resistance also improved with filler loading up to 30 wt%, and then dwindled significantly with 40 wt% and 50 wt% of the filler. Consequently, the sample with 10 wt% filler had the highest tensile strength of 48 MPa; while, sample with 50 wt% of filler had least tensile strength of 20.9 MPa. Again, impact strength result showed that the sample with 10% wt had superior impact strength of 0.45 J/mm. Scanning electron microscopy image of the fractured tensile specimen further highlighted the reason for the improved mechanical properties recorded at 10 wt%. The results suggest that the baobab fiber nano-composite had adequate properties for application in the automotive industry and building construction.