Exploiting Synergistic Experimental and Computational Approaches to Design and Fabricate High-Performance Elastomer
Guanyi Hou,Xinlei Zhou,Sai Li,Ruifeng Jiang,Zhiyu Zhang,Mengjie Dong,Jun Liu,Yonglai Lu,Wencai Wang,Liqun Zhang,Shihu Wang
DOI: https://doi.org/10.1021/acs.macromol.0c01285
IF: 5.5
2020-07-30
Macromolecules
Abstract:Silicone elastomers (SRs) are of great scientific and technological importance due to their resistance to low temperatures. However, the glass transition temperature (<i>T</i><sub>g</sub>) of existing SRs is not low enough to satisfy its utilization in the extremely low-temperature environment. Meanwhile, crystallization often occurs at the low-temperature, making it difficult for SRs to maintain their original properties in the extremely low-temperature environment. Here, by combining molecular dynamics (MD) simulation and experiment, a novel low-temperature resistance and crystalline-free SR (Epoxidized-Methyl-Ethyl-Vinyl Silicone Elastomer, also referred to E-MEVQ) is fabricated by random copolymerization of three different siloxane repeat units (dimethyl-siloxane, diethyl-siloxane and methyl-epoxy-siloxane). We showed that the <i>T</i><sub>g</sub> of E-MEVQ computed from MD simulations using three different methods (specific volume, nonbond potential energy and conformational transition versus temperature) agrees well with that of the as-synthesized E-MEVQ determined by Differential Scanning Calorimetry. The <i>T</i><sub>g</sub> is approximately −130 °C, much lower than that of Polydimethylsiloxane (PDMS), and the E-MEVQ is in the amorphous state without any crystallization. This novel silicone elastomer is expected to be widely applied in the field of smart devices, sensors, and medical equipment under extreme situations. Our work also provides a promising framework for designing and fabricating high-performance elastomeric polymer materials via simulation and experiment.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.macromol.0c01285?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.macromol.0c01285</a>.Table S1, List of raw materials and agents; Table S2, each group percentage for E-MEVQ with different epoxy group percentage; Table S3, chemical shift and the corresponding group name; Figure S1, reaction formula of TMAOH-Si; Figure S2, reaction formula of MEVQ; Figure S3, reaction formula of epoxy modification; Figure S4, specific volume as a function of temperature; Figure S5, non-bond potential energy; Figure S6, <i>K</i><sub>T</sub> as a function of temperature; Figure S7, distribution of the dihedral angle (Si–O–Si–O) at −185.15 °C; Figure S8, FT–IR spectra of E-MEVQ; and Figure S9, <sup>1</sup>H-NMR spectra of E-MEVQ (<a class="ext-link" href="/doi/suppl/10.1021/acs.macromol.0c01285/suppl_file/ma0c01285_si_001.mp4">MP4</a>)Movie S1, Compression progress of commercial PDMS cylinder in −70 °C (<a class="ext-link" href="/doi/suppl/10.1021/acs.macromol.0c01285/suppl_file/ma0c01285_si_002.mp4">MP4</a>)Movie S2, Compression progress of E-MEVQ with 5% epoxy groups cylinder in −70 °C (<a class="ext-link" href="/doi/suppl/10.1021/acs.macromol.0c01285/suppl_file/ma0c01285_si_003.pdf">PDF</a>)This article has not yet been cited by other publications.
polymer science