One-Pot Hydrothermal Synthesis of Nickel Cobalt Telluride Nanorods for Hybrid Energy Storage Systems
M. Manikandan,K. Subramani,S. Dhanuskodi,M. Sathish
DOI: https://doi.org/10.1021/acs.energyfuels.1c00351
2021-05-06
Abstract:Herein, we delineate the one-pot preparation of nickel cobalt telluride nanorods (NiCoTe NRs) by the hydrothermal method using cetyltrimethylammonium bromide and ascorbic acid as reducing agents. The Ni<sub>0.7</sub>Co<sub>0.3</sub>Te NRs (NCT-1 NRs) were investigated with different characterization techniques, such as X-ray diffraction, field emission scanning electron microscopy, transmission electron microscopy, and X-ray photoelectron spectroscopy. Magnetic measurement shows the paramagnetic behavior of the prepared samples with the saturation magnetization. The NCT-1 NR-modified electrode is employed into the electrochemical hydrogen evolution reaction and hybrid supercapacitor applications. NCT-1 is demonstrated as a good electrocatalyst for the hydrogen evolution reaction at the onset potential of 244 mV versus reversible hydrogen electrode and delivered a high current density of 1 mA/cm<sup>2</sup>. NCT-1 displays a specific capacity of 433 C/g at 0.5 A/g current density and 100% capacity retention, even after 5000 cycles. Furthermore, a hybrid asymmetric supercapacitor device was fabricated on the basis of NCT-1 as a positive electrode and orange-peel-derived activated carbon (OPC-700) as a negative electrode. It delivered a high energy density of 43 Wh/kg and a power density of 905 W/kg with long cyclic stability of 91% after 25 000 cycles.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.energyfuels.1c00351?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.energyfuels.1c00351</a>.Detailed experimental section with material characterization and electrochemical measurements for supercapacitor studies and hybrid asymmetric cell fabrication, FESEM images of NCT-1, NCT-2, and NCT-3 (Figure S1), BET isotherm of NCT-3 (Figure S2), FESEM and EDS spectrum of NCT-1 before and after the stability test (Figure S3), CV and GCD profile of NCT-2 and NCT-3 (Figure S4), specific capacity of all materials versus current density curve from half cell and full cell (Figure S5), cyclic stability test for NCT-2 and NCT-3 electrodes (Figure S6), specific capacity as a function of the current density plot of NCT-1||OPC-700 ASC (Figure S7), detailed magnetic properties of NCT samples at different temperatures (Table S1), and comparison of electrochemical properties of metal-chalcogenide-based ASCs (Table S2) (<a class="ext-link" href="/doi/suppl/10.1021/acs.energyfuels.1c00351/suppl_file/ef1c00351_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
energy & fuels,engineering, chemical